The Charpy impact test, also known as the Charpy v-notch test, is a standardized high strain-rate test which determines the amount of energy absorbed by a material during fracture. This absorbed energy is a measure of a given material's toughness and acts as a tool to study temperature-dependent brittle-ductile transition. It is widely applied in industry, since it is easy to prepare and conduct and results can be obtained quickly and cheaply. But a major disadvantage is that all results are only comparative.[1]

The test was developed in 1905 by the French scientist Georges Charpy. It was pivotal in understanding the fracture problems of ships during the Second World War. Today it is used in many industries for testing building and construction materials used in the construction of pressure vessels, bridges and to see how storms will affect materials used in building.[2]

Contents

Definition

A vintage impact test machine.

The apparatus consists of a pendulum axe swinging at a notched sample of material. The energy transferred to the material can be inferred by comparing the difference in the height of the hammer before and after a big fracture.

The notch in the sample affects the results of the impact test,[3] thus it is necessary for the notch to be of regular dimensions and geometry. The size of the sample can also affect results, since the dimensions determine whether or not the material is in plane strain. This difference can greatly affect conclusions made.[4]

The "Standard methods for Notched Bar Impact Testing of Metallic Materials" can be found in ASTM E23[5], ISO 148-1[6] or EN 10045-1[7], where all the aspects of the test and equipment used are described in detail.

Quantitative results

The quantitative result of the impact tests the energy needed to fracture a material and can be used to measure the toughness of the material and the yield strength. Also, the strain rate may be studied and analyzed for its effect on fracture.

The ductile-brittle transition temperature (DBTT) may be derived from the temperature where the energy needed to fracture the material drastically changes. However, in practice there is no sharp transition and so it is difficult to obtain a precise transition temperature. An exact DBTT may be empirically derived in many ways: a specific absorbed energy, change in aspect of fracture (such as 50% of the area is cleavage), etc.[1]

Qualitative results

The qualitative results of the impact test can be used to determine the ductility of a material.[8] If the material breaks on a flat plane, the fracture was brittle, and if the material breaks with jagged edges or shear lips, then the fracture was ductile. Usually a material does not break in just one way or the other, and thus comparing the jagged to flat surface areas of the fracture will give an estimate of the percentage of ductile and brittle fracture.[1]

Sample sizes

According to ASTM A370,[9] the standard specimen size for Charpy impact testing is 10mm×10mm×55mm. Subsize specimen sizes are: 10mm×7.5mm×55mm, 10mm×6.7mm×55mm, 10mm×5mm×55mm, 10mm×3.3mm×55mm, 10mm×2.5mm×55mm. Details of specimens as per ASTM A370 (Standard Test Method and Definitions for Mechanical Testing of Steel Products).

According to EN 10045-1,[7] standard specimen sizes are 10mmx10mmx55mm. Subsize specimens are: 10mmx7.5mmx55mm and 10mmx5mmx55mm.

See also

Notes

  1. ^ a b c Meyers Marc A, Chawla Krishan Kumar (1998). Mechanical Behaviors of Materials. Prentice Hall. ISBN 9780132628174. 
  2. ^ Jacobs James A, Kilduff Thomas F (2005). Engineering Materials Technology (5th ed.). Pearson Prentice Hall. pp. 153–155. ISBN 9780130481856. 
  3. ^ Kurishita H, Kayano H, Narui M, Yamazaki M, Kano Y, Shibahara I (1993). "Effects of V-notch dimensions on Charpy impact test results for differently sized miniature specimens of ferritic steel". Materials Transactions - JIM (Japan Institute of Metals) 34 (11): 1042–52. ISSN 0916-1821. 
  4. ^ Mills NJ (February 1976). "The mechanism of brittle fracture in notched impact tests on polycarbonate". Journal of Materials Science 11 (2): 363–75. Bibcode 1976JMatS..11..363M. doi:10.1007/BF00551448. 
  5. ^ ASTM E23 Standard Test Methods for Notched Bar Impact Testing of Metallic Materials
  6. ^ ISO 148-1 Metallic materials - Charpy pendulum impact test - Part 1: Test method
  7. ^ a b EN 10045-1 Charpy impact test on metallic materials. Test method (V- and U-notches)
  8. ^ Mathurt KK, Needleman A, Tvergaard V (May 1994). "3D analysis of failure modes in the Charpy impact test". Modeling and Simulation in Materials Science Engineering 2 (3A): 617–35. Bibcode 1994MSMSE...2..617M. doi:10.1088/0965-0393/2/3A/014. 
  9. ^ ASTM A370 Standard Test Methods and Definitions for Mechanical Testing of Steel Products

External links


Wikimedia Foundation. 2010.

Look at other dictionaries:

  • Charpy impact test — noun A test of the impact strength of a material, used to determine its relative ductility or brittleness. The test is executed by swinging a large, heavy hammer on a pendulum from a predetermined height. The hammer fractures the material sample …   Wiktionary

  • impact test — Test of the ability of a material to withstand impact, used by engineers to predict its behaviour under actual conditions. Many materials fail suddenly under impact, at flaws, cracks, or notches. The most common impact tests use a swinging… …   Universalium

  • impact test — a test designed to give information on how a specimen of a known material will respond to a suddenly applied stress, e.g. shock. The test ascertains whether the material is tough or brittle. A notched test piece is normally employed and the two… …   Mechanics glossary

  • pendulum impact test — The standard test methods are the Izod and Charpy tests; the specimens have a standard notch machined in them, and the impact energy absorbed in breaking the specimen is recorded …   Dictionary of automotive terms

  • Impact force — An impact force is a high force or shock applied over a short time period. Such a force or acceleration can sometimes have a greater effect than a lower force applied over a proportionally longer time period. Theory At normal speeds, during a… …   Wikipedia

  • test — See acceptance test bench test bend test board test brake test breathalyzer test breath test car test charpy test crash test …   Dictionary of automotive terms

  • test — bend test Brinell hardness test Charpy test creep test cup test diamond pyramid hardnesstest elongation test end quench test endurance test impact test Izod impact test Jominy test …   Mechanics glossary

  • Charpy test — a test to measure the impact properties of steel. A prepared test piece, usually notched, is broken by a swinging pendulum. The energy consumed in breaking the test piece is measured in Joules. The more brittle the steel the lower the impact… …   Mechanics glossary

  • Charpy test — An impact resistance test in which the specimen is supported as a horizontal beam and broken by a single swing of a pendulum with the impact line midway between the supports and directly opposite the notch for notched specimens …   Dictionary of automotive terms

  • Izod impact strength test — Izod impact strength testing is an ASTM standard method of determining impact strength. A notched sample is generally used to determine impact strength.The test is named after the English engineer Edwin Gilbert Izod (1876 1946), who described it… …   Wikipedia


Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”

We are using cookies for the best presentation of our site. Continuing to use this site, you agree with this.