- Carbon nanotube
Part of a series of articles on
Carbon nanotubes (CNTs) are allotropes of carbon with a cylindrical nanostructure. Nanotubes have been constructed with length-to-diameter ratio of up to 132,000,000:1, significantly larger than for any other material. These cylindrical carbon molecules have unusual properties, which are valuable for nanotechnology, electronics, optics and other fields of materials science and technology. In particular, owing to their extraordinary thermal conductivity and mechanical and electrical properties, carbon nanotubes may find applications as additives to various structural materials.
Nanotubes are members of the fullerene structural family, which also includes the spherical buckyballs, and the ends of a nanotube may be capped with a hemisphere of the buckyball structure. Their name is derived from their long, hollow structure with the walls formed by one-atom-thick sheets of carbon, called graphene. These sheets are rolled at specific and discrete ("chiral") angles, and the combination of the rolling angle and radius decides the nanotube properties; for example, whether the individual nanotube shell is a metal or semiconductor. Nanotubes are categorized as single-walled nanotubes (SWNTs) and multi-walled nanotubes (MWNTs). Individual nanotubes naturally align themselves into "ropes" held together by van der Waals forces, more specifically, pi-stacking.
Applied quantum chemistry, specifically, orbital hybridization best describes chemical bonding in nanotubes. The chemical bonding of nanotubes is composed entirely of sp2 bonds, similar to those of graphite. These bonds, which are stronger than the sp3 bonds found in alkanes, provide nanotubules with their unique strength.
- 1 Types of carbon nanotubes and related structures
- 2 Properties
- 3 Synthesis
- 4 Current applications
- 5 Potential applications
- 6 Discovery
- 7 See also
- 8 References
- 9 Free-download reviews
- 10 External links
There is no consensus on some terms describing carbon nanotubes in scientific literature: both "-wall" and "-walled" are being used in combination with "single", "double", "triple" or "multi", and the letter C is often omitted in the abbreviation; for example, multi-walled carbon nanotube (MWNT).
Most single-walled nanotubes (SWNT) have a diameter of close to 1 nanometer, with a tube length that can be many millions of times longer. The structure of a SWNT can be conceptualized by wrapping a one-atom-thick layer of graphite called graphene into a seamless cylinder. The way the graphene sheet is wrapped is represented by a pair of indices (n,m) . The integers n and m denote the number of unit vectors along two directions in the honeycomb crystal lattice of graphene. If m = 0, the nanotubes are called zigzag nanotubes, and if n = m, the nanotubes are called armchair nanotubes. Otherwise, they are called chiral. The diameter of an ideal nanotube can be calculated from its (n,m) indices as follows
where a = 0.246 nm.
SWNTs are an important variety of carbon nanotube because most of their properties change significantly with the (n,m) values, and this dependence is non-monotonic (see Kataura plot). In particular, their band gap can vary from zero to about 2 eV and their electrical conductivity can show metallic or semiconducting behavior. One useful application of SWNTs is in the development of the first intramolecular field-effect transistors (FET). Production of the first intramolecular logic gate using SWNT FETs has recently become possible as well. To create a logic gate you must have both a p-FET and an n-FET. Because SWNTs are p-FETs when exposed to oxygen and n-FETs otherwise, it is possible to protect half of an SWNT from oxygen exposure, while exposing the other half to oxygen. This results in a single SWNT that acts as a NOT logic gate with both p and n-type FETs within the same molecule.
Single-walled nanotubes are dropping precipitously in price, from around $1500 per gram as of 2000 to retail prices of around $50 per gram of as-produced 40–60% by weight SWNTs as of March 2010.
Multi-walled nanotubes (MWNT) consist of multiple rolled layers (concentric tubes) of graphite. There are two models that can be used to describe the structures of multi-walled nanotubes. In the Russian Doll model, sheets of graphite are arranged in concentric cylinders, e.g., a (0,8) single-walled nanotube (SWNT) within a larger (0,17) single-walled nanotube. In the Parchment model, a single sheet of graphite is rolled in around itself, resembling a scroll of parchment or a rolled newspaper. The interlayer distance in multi-walled nanotubes is close to the distance between graphene layers in graphite, approximately 3.4 Å. The Russian Doll structure is observed more commonly. Its individual shells can be described as SWNTs, which can be metallic or semiconducting. Because of statistical probability and restrictions on the relative diameters of the individual tubes, one of the shells, and thus the whole MWNT, is usually a zero-gap metal.
Double-walled carbon nanotubes (DWNT) form a special class of nanotubes because their morphology and properties are similar to those of SWNT but their resistance to chemicals is significantly improved. This is especially important when functionalization is required (this means grafting of chemical functions at the surface of the nanotubes) to add new properties to the CNT. In the case of SWNT, covalent functionalization will break some C=C double bonds, leaving "holes" in the structure on the nanotube and, thus, modifying both its mechanical and electrical properties. In the case of DWNT, only the outer wall is modified. DWNT synthesis on the gram-scale was first proposed in 2003 by the CCVD technique, from the selective reduction of oxide solutions in methane and hydrogen.
The telescopic motion ability of inner shells  and their unique mechanical properties  permit to use multi-walled nanotubes as main movable arms in coming nanomechanical devices. Retraction force that occurs to telescopic motion caused by the Lennard-Johnes interaction between shells and its value is about 1.5 nN.
In theory, a nanotorus is a carbon nanotube bent into a torus (doughnut shape). Nanotori are predicted to have many unique properties, such as magnetic moments 1000 times larger than previously expected for certain specific radii. Properties such as magnetic moment, thermal stability, etc. vary widely depending on radius of the torus and radius of the tube.
Carbon nanobuds are a newly created material combining two previously discovered allotropes of carbon: carbon nanotubes and fullerenes. In this new material, fullerene-like "buds" are covalently bonded to the outer sidewalls of the underlying carbon nanotube. This hybrid material has useful properties of both fullerenes and carbon nanotubes. In particular, they have been found to be exceptionally good field emitters. In composite materials, the attached fullerene molecules may function as molecular anchors preventing slipping of the nanotubes, thus improving the composite’s mechanical properties.
Cup stacked carbon nanotubes
Cup-stacked carbon nanotubes (CSCNTs) differ from other quasi-1D carbon structures, which normally behave as quasi-metallic conductors of electrons. CSCNTs exhibit semiconducting behaviors due to the stacking microstructure of graphene layers.
Extreme carbon nanotubes
The observation of the longest carbon nanotubes (18.5 cm long) was reported in 2009. These nanotubes were grown on Si substrates using an improved chemical vapor deposition (CVD) method and represent electrically uniform arrays of single-walled carbon nanotubes.
The thinnest carbon nanotube is armchair (2,2) CNT with a diameter of 3 Å. This nanotube was grown inside a multi-walled carbon nanotube. Assigning of carbon nanotube type was done by combination of high-resolution transmission electron microscopy (HRTEM), Raman spectroscopy and density functional theory (DFT) calculations.
The thinnest freestanding single-walled carbon nanotube is about 4.3 Å in diameter. Researchers suggested that it can be either (5,1) or (4,2) SWCNT, but exact type of carbon nanotube remains questionable. (3,3), (4,3) and (5,1) carbon nanotubes (all about 4 Å in diameter) were unambiguously identified using more precise aberration-corrected high-resolution transmission electron microscopy. However, they were found inside of double-walled carbon nanotubes.
Carbon nanotubes are the strongest and stiffest materials yet discovered in terms of tensile strength and elastic modulus respectively. This strength results from the covalent sp2 bonds formed between the individual carbon atoms. In 2000, a multi-walled carbon nanotube was tested to have a tensile strength of 63 gigapascals (GPa). (For illustration, this translates into the ability to endure tension of a weight equivalent to 6422 kg on a cable with cross-section of 1 mm2.) Further studies, conducted in 2008, revealed that individual CNT shells have strengths of up to ~100 GPa, which is in good agreement with quantum/atomistic models. Since carbon nanotubes have a low density for a solid of 1.3 to 1.4 g/cm3, its specific strength of up to 48,000 kN·m·kg−1 is the best of known materials, compared to high-carbon steel's 154 kN·m·kg−1.
Under excessive tensile strain, the tubes will undergo plastic deformation, which means the deformation is permanent. This deformation begins at strains of approximately 5% and can increase the maximum strain the tubes undergo before fracture by releasing strain energy.
Although the strength of individual CNT shells is extremely high, weak shear interactions between adjacent shells and tubes leads to significant reductions in the effective strength of multi-walled carbon nanotubes and carbon nanotube bundles down to only a few GPa’s. This limitation has been recently addressed by applying high-energy electron irradiation, which crosslinks inner shells and tubes, and effectively increases the strength of these materials to ~60 GPa for multi-walled carbon nanotubes and ~17 GPa for double-walled carbon nanotube bundles.
CNTs are not nearly as strong under compression. Because of their hollow structure and high aspect ratio, they tend to undergo buckling when placed under compressive, torsional, or bending stress.
Comparison of mechanical properties Material Young's modulus (TPa) Tensile strength (GPa) Elongation at break (%) SWNTE ~1 (from 1 to 5) 13–53 16 Armchair SWNTT 0.94 126.2 23.1 Zigzag SWNTT 0.94 94.5 15.6–17.5 Chiral SWNT 0.92 MWNTE 0.2–0.8–0.95 11–63–150 Stainless steelE 0.186–0.214 0.38–1.55 15–50 Kevlar–29&149E 0.06–0.18 3.6–3.8 ~2
EExperimental observation; TTheoretical prediction
The above discussion referred to axial properties of the nanotube, whereas simple geometrical considerations suggest that carbon nanotubes should be much softer in the radial direction than along the tube axis. Indeed, TEM observation of radial elasticity suggested that even the van der Waals forces can deform two adjacent nanotubes. Nanoindentation experiments, performed by several groups on multiwalled carbon nanotubes  and tapping/contact mode atomic force microscope measurement performed on single-walled carbon nanotube, indicated Young's modulus of the order of several GPa confirming that CNTs are indeed rather soft in the radial direction.
Standard single-walled carbon nanotubes can withstand a pressure up to 24GPa without deformation. They then undergo a transformation to superhard phase nanotubes. Maximum pressures measured using current experimental techniques are around 55GPa. However, these new superhard phase nanotubes collapse at an even higher, albeit unknown, pressure.
Multi-walled nanotubes are multiple concentric nanotubes precisely nested within one another. These exhibit a striking telescoping property whereby an inner nanotube core may slide, almost without friction, within its outer nanotube shell, thus creating an atomically perfect linear or rotational bearing. This is one of the first true examples of molecular nanotechnology, the precise positioning of atoms to create useful machines. Already, this property has been utilized to create the world's smallest rotational motor. Future applications such as a gigahertz mechanical oscillator are also envisaged.
Because of the symmetry and unique electronic structure of graphene, the structure of a nanotube strongly affects its electrical properties. For a given (n,m) nanotube, if n = m, the nanotube is metallic; if n − m is a multiple of 3, then the nanotube is semiconducting with a very small band gap, otherwise the nanotube is a moderate semiconductor. Thus all armchair (n = m) nanotubes are metallic, and nanotubes (6,4), (9,1), etc. are semiconducting.
However, this rule has exceptions, because curvature effects in small diameter carbon nanotubes can strongly influence electrical properties. Thus, a (5,0) SWCNT that should be semiconducting in fact is metallic according to the calculations. Likewise, vice versa-- zigzag and chiral SWCNTs with small diameters that should be metallic have finite gap (armchair nanotubes remain metallic). In theory, metallic nanotubes can carry an electric current density of 4 × 109 A/cm2, which is more than 1,000 times greater than those of metals such as copper, where for copper interconnects current densities are limited by electromigration.
Multiwalled carbon nanotubes with interconnected inner shells show superconductivity with a relatively high transition temperature Tc = 12 K. In contrast, the Tc value is an order of magnitude lower for ropes of single-walled carbon nanotubes or for MWNTs with usual, non-interconnected shells.
All nanotubes are expected to be very good thermal conductors along the tube, exhibiting a property known as "ballistic conduction", but good insulators laterally to the tube axis. Measurements show that a SWNT has a room-temperature thermal conductivity along its axis of about 3500 W·m−1·K−1; compare this to copper, a metal well known for its good thermal conductivity, which transmits 385 W·m−1·K−1. A SWNT has a room-temperature thermal conductivity across its axis (in the radial direction) of about 1.52 W·m−1·K−1, which is about as thermally conductive as soil. The temperature stability of carbon nanotubes is estimated to be up to 2800 °C in vacuum and about 750 °C in air.
As with any material, the existence of a crystallographic defect affects the material properties. Defects can occur in the form of atomic vacancies. High levels of such defects can lower the tensile strength by up to 85%. An important example is the Stone Wales defect, which creates a pentagon and heptagon pair by rearrangement of the bonds. Because of the very small structure of CNTs, the tensile strength of the tube is dependent on its weakest segment in a similar manner to a chain, where the strength of the weakest link becomes the maximum strength of the chain.
Crystallographic defects also affect the tube's electrical properties. A common result is lowered conductivity through the defective region of the tube. A defect in armchair-type tubes (which can conduct electricity) can cause the surrounding region to become semiconducting, and single monoatomic vacancies induce magnetic properties.
Crystallographic defects strongly affect the tube's thermal properties. Such defects lead to phonon scattering, which in turn increases the relaxation rate of the phonons. This reduces the mean free path and reduces the thermal conductivity of nanotube structures. Phonon transport simulations indicate that substitutional defects such as nitrogen or boron will primarily lead to scattering of high-frequency optical phonons. However, larger-scale defects such as Stone Wales defects cause phonon scattering over a wide range of frequencies, leading to a greater reduction in thermal conductivity.
Because of the nanoscale dimensions, electrons propagate only along the tube's axis and electron transport involves many quantum effects. Because of this, carbon nanotubes are frequently referred to as “one-dimensional”.
The toxicity of carbon nanotubes has been an important question in nanotechnology. Such research has just begun. The data are still fragmentary and subject to criticism. Preliminary results highlight the difficulties in evaluating the toxicity of this heterogeneous material. Parameters such as structure, size distribution, surface area, surface chemistry, surface charge, and agglomeration state as well as purity of the samples, have considerable impact on the reactivity of carbon nanotubes. However, available data clearly show that, under some conditions, nanotubes can cross membrane barriers, which suggests that, if raw materials reach the organs, they can induce harmful effects such as inflammatory and fibrotic reactions.
Results of rodent studies collectively show that regardless of the process by which CNTs were synthesized and the types and amounts of metals they contained, CNTs were capable of producing inflammation, epithelioid granulomas (microscopic nodules), fibrosis, and biochemical/toxicological changes in the lungs. Comparative toxicity studies in which mice were given equal weights of test materials showed that SWCNTs were more toxic than quartz, which is considered a serious occupational health hazard when chronically inhaled. As a control, ultrafine carbon black was shown to produce minimal lung responses.
The needle-like fiber shape of CNTs is similar to asbestos fibers. This raises the idea that widespread use of carbon nanotubes may lead to pleural mesothelioma, a cancer of the lining of the lungs or peritoneal mesothelioma, a cancer of the lining of the abdomen (both caused by exposure to asbestos). A recently-published pilot study supports this prediction. Scientists exposed the mesothelial lining of the body cavity of mice to long multiwalled carbon nanotubes and observed asbestos-like, length-dependent, pathogenic behavior that included inflammation and formation of lesions known as granulomas. Authors of the study conclude:
- "This is of considerable importance, because research and business communities continue to invest heavily in carbon nanotubes for a wide range of products under the assumption that they are no more hazardous than graphite. Our results suggest the need for further research and great caution before introducing such products into the market if long-term harm is to be avoided."
According to co-author Dr. Andrew Maynard:
- "This study is exactly the kind of strategic, highly focused research needed to ensure the safe and responsible development of nanotechnology. It looks at a specific nanoscale material expected to have widespread commercial applications and asks specific questions about a specific health hazard. Even though scientists have been raising concerns about the safety of long, thin carbon nanotubes for over a decade, none of the research needs in the current U.S. federal nanotechnology environment, health and safety risk research strategy address this question."
Although further research is required, the available data suggests that under certain conditions, especially those involving chronic exposure, carbon nanotubes can pose a serious risk to human health.
Techniques have been developed to produce nanotubes in sizeable quantities, including arc discharge, laser ablation, high-pressure carbon monoxide (HiPco), and chemical vapor deposition (CVD). Most of these processes take place in vacuum or with process gases. CVD growth of CNTs can occur in vacuum or at atmospheric pressure. Large quantities of nanotubes can be synthesized by these methods; advances in catalysis and continuous growth processes are making CNTs more commercially viable.
Nanotubes were observed in 1991 in the carbon soot of graphite electrodes during an arc discharge, by using a current of 100 amps, that was intended to produce fullerenes. However the first macroscopic production of carbon nanotubes was made in 1992 by two researchers at NEC's Fundamental Research Laboratory. The method used was the same as in 1991. During this process, the carbon contained in the negative electrode sublimates because of the high-discharge temperatures. Because nanotubes were initially discovered using this technique, it has been the most widely-used method of nanotube synthesis.
The yield for this method is up to 30% by weight and it produces both single- and multi-walled nanotubes with lengths of up to 50 micrometers with few structural defects.
In the laser ablation process, a pulsed laser vaporizes a graphite target in a high-temperature reactor while an inert gas is bled into the chamber. Nanotubes develop on the cooler surfaces of the reactor as the vaporized carbon condenses. A water-cooled surface may be included in the system to collect the nanotubes.
This process was developed by Dr. Richard Smalley and co-workers at Rice University, who at the time of the discovery of carbon nanotubes, were blasting metals with a laser to produce various metal molecules. When they heard of the existence of nanotubes they replaced the metals with graphite to create multi-walled carbon nanotubes. Later that year the team used a composite of graphite and metal catalyst particles (the best yield was from a cobalt and nickel mixture) to synthesize single-walled carbon nanotubes.
The laser ablation method yields around 70% and produces primarily single-walled carbon nanotubes with a controllable diameter determined by the reaction temperature. However, it is more expensive than either arc discharge or chemical vapor deposition.
Chemical vapor deposition (CVD)
The catalytic vapor phase deposition of carbon was first reported in 1959, but it was not until 1993 that carbon nanotubes were formed by this process. In 2007, researchers at the University of Cincinnati (UC) developed a process to grow aligned carbon nanotube arrays of 18 mm length on a FirstNano ET3000 carbon nanotube growth system.
During CVD, a substrate is prepared with a layer of metal catalyst particles, most commonly nickel, cobalt, iron, or a combination. The metal nanoparticles can also be produced by other ways, including reduction of oxides or oxides solid solutions. The diameters of the nanotubes that are to be grown are related to the size of the metal particles. This can be controlled by patterned (or masked) deposition of the metal, annealing, or by plasma etching of a metal layer. The substrate is heated to approximately 700°C. To initiate the growth of nanotubes, two gases are bled into the reactor: a process gas (such as ammonia, nitrogen or hydrogen) and a carbon-containing gas (such as acetylene, ethylene, ethanol or methane). Nanotubes grow at the sites of the metal catalyst; the carbon-containing gas is broken apart at the surface of the catalyst particle, and the carbon is transported to the edges of the particle, where it forms the nanotubes. This mechanism is still being studied. The catalyst particles can stay at the tips of the growing nanotube during the growth process, or remain at the nanotube base, depending on the adhesion between the catalyst particle and the substrate. Thermal catalytic decomposition of hydrocarbon has become an active area of research and can be a promising route for the bulk production of CNTs. Fluidised bed reactor is the most widely used reactor for CNT preparation. Scale-up of the reactor is the major challenge. 
CVD is a common method for the commercial production of carbon nanotubes. For this purpose, the metal nanoparticles are mixed with a catalyst support such as MgO or Al2O3 to increase the surface area for higher yield of the catalytic reaction of the carbon feedstock with the metal particles. One issue in this synthesis route is the removal of the catalyst support via an acid treatment, which sometimes could destroy the original structure of the carbon nanotubes. However, alternative catalyst supports that are soluble in water have proven effective for nanotube growth.
If a plasma is generated by the application of a strong electric field during the growth process (plasma enhanced chemical vapor deposition), then the nanotube growth will follow the direction of the electric field. By adjusting the geometry of the reactor it is possible to synthesize vertically aligned carbon nanotubes (i.e., perpendicular to the substrate), a morphology that has been of interest to researchers interested in the electron emission from nanotubes. Without the plasma, the resulting nanotubes are often randomly oriented. Under certain reaction conditions, even in the absence of a plasma, closely spaced nanotubes will maintain a vertical growth direction resulting in a dense array of tubes resembling a carpet or forest.
Of the various means for nanotube synthesis, CVD shows the most promise for industrial-scale deposition, because of its price/unit ratio, and because CVD is capable of growing nanotubes directly on a desired substrate, whereas the nanotubes must be collected in the other growth techniques. The growth sites are controllable by careful deposition of the catalyst. In 2007, a team from Meijo University demonstrated a high-efficiency CVD technique for growing carbon nanotubes from camphor. Researchers at Rice University, until recently led by the late Richard Smalley, have concentrated upon finding methods to produce large, pure amounts of particular types of nanotubes. Their approach grows long fibers from many small seeds cut from a single nanotube; all of the resulting fibers were found to be of the same diameter as the original nanotube and are expected to be of the same type as the original nanotube.
Super-growth CVD (water-assisted chemical vapor deposition) process was developed by Kenji Hata, Sumio Iijima and co-workers at AIST, Japan. In this process, the activity and lifetime of the catalyst are enhanced by addition of water into the CVD reactor. Dense millimeter-tall nanotube "forests", aligned normal to the substrate, were produced. The forests growth rate could be expressed, as
In this equation, β is the initial growth rate and τo is the characteristic catalyst lifetime.
Their specific surface exceeds 1,000 m2/g (capped) or 2,200 m2/g (uncapped), surpassing the value of 400–1,000 m2/g for HiPco samples. The synthesis efficiency is about 100 times higher than for the laser ablation method. The time required to make SWNT forests of the height of 2.5 mm by this method was 10 minutes in 2004. Those SWNT forests can be easily separated from the catalyst, yielding clean SWNT material (purity >99.98%) without further purification. For comparison, the as-grown HiPco CNTs contain about 5–35% of metal impurities; it is therefore purified through dispersion and centrifugation that damages the nanotubes. The super-growth process avoids this problem. Patterned highly organized single-walled nanotube structures were successfully fabricated using the super-growth technique.
The mass density of super-growth CNTs is about 0.037 g/cm3. It is much lower than that of conventional CNT powders (~1.34 g/cm3), probably because the latter contain metals and amorphous carbon.
The super-growth method is basically a variation of CVD. Therefore, it is possible to grow material containing SWNT, DWNTs and MWNTs, and to alter their ratios by tuning the growth conditions. Their ratios change by the thinness of the catalyst. Many MWNTs are included so that the diameter of the tube is wide.
The vertically aligned nanotube forests originate from a "zipping effect" when they are immersed in a solvent and dried. The zipping effect is caused by the surface tension of the solvent and the van der Waals forces between the carbon nanotubes. It aligns the nanotubes into a dense material, which can be formed in various shapes, such as sheets and bars, by applying weak compression during the process. Densification increases the Vickers hardness by about 70 times and density is 0.55 g/cm3. The packed carbon nanotubes are more than 1 mm long and have a carbon purity of 99.9% or higher; they also retain the desirable alignment properties of the nanotubes forest.
Natural, incidental, and controlled flame environments
Fullerenes and carbon nanotubes are not necessarily products of high-tech laboratories; they are commonly formed in such mundane places as ordinary flames, produced by burning methane, ethylene, and benzene, and they have been found in soot from both indoor and outdoor air. However, these naturally occurring varieties can be highly irregular in size and quality because the environment in which they are produced is often highly uncontrolled. Thus, although they can be used in some applications, they can lack in the high degree of uniformity necessary to satisfy the many needs of both research and industry. Recent efforts have focused on producing more uniform carbon nanotubes in controlled flame environments. Such methods have promise for large-scale, low-cost nanotube synthesis, though they must compete with rapidly developing large scale CVD production.
Many electronic applications of carbon nanotubes crucially rely on techniques of selectively producing either semiconducting or metallic CNTs, preferably of a certain chirality. Several methods of separating semiconducting and metallic CNTs are known, but most of them are not yet suitable for large-scale technological processes. The most efficient method relies on density-gradient ultracentrifugation, which separates surfactant-wrapped nanotubes by the minute difference in their density. This density difference often translates into difference in the nanotube diameter and (semi)conducting properties. Another method of separation uses a sequence of freezing, thawing, and compression of SWNTs embedded in agarose gel. This process results in a solution containing 70% metallic SWNTs and leaves a gel containing 95% semiconducting SWNTs. The diluted solutions separated by this method show various colors. Moreover, SWNTs can be separated by the column chromatography method. Yield is 95% in semiconductor type SWNT and 90% in metallic type SWNT.
In addition to separation of semiconducting and metallic SWNTs, it is possible to sort SWNTs by length, diameter, and chirality. The highest resolution length sorting, with length variation of <10%, has thus far been achieved by size exclusion chromatography (SEC) of DNA-dispersed carbon nanotubes (DNA-SWNT). SWNT diameter separation has been achieved by density-gradient ultracentrifugation (DGU) using surfactant-dispersed SWNTs and by ion-exchange chromatography (IEC) for DNA-SWNT. Purification of individual chiralities has also been demonstrated with IEC of DNA-SWNT: specific short DNA oligomers can be used to isolate individual SWNT chiralities. Thus far, 12 chiralities have been isolated at purities ranging from 70% for (8,3) and (9,5) SWNTs to 90% for (6,5), (7,5) and (10,5)SWNTs. There have been successful efforts to integrate these purified nanotubes into devices, e. g. FETs.
An alternative to separation is development of a selective growth of semiconducting or metallic CNTs. Recently, a new CVD recipe that involves a combination of ethanol and methanol gases and quartz substrates resulting in horizontally aligned arrays of 95–98% semiconducting nanotubes was announced.
Nanotubes are usually grown on nanoparticles of magnetic metal (Fe, Co), which facilitates production of electronic (spintronic) devices. In particular, control of current through a field-effect transistor by magnetic field has been demonstrated in such a single-tube nanostructure.
Current use and application of nanotubes has mostly been limited to the use of bulk nanotubes, which is a mass of rather unorganized fragments of nanotubes. Bulk nanotube materials may never achieve a tensile strength similar to that of individual tubes, but such composites may, nevertheless, yield strengths sufficient for many applications. Bulk carbon nanotubes have already been used as composite fibers in polymers to improve the mechanical, thermal and electrical properties of the bulk product.
- Easton-Bell Sports, Inc. have been in partnership with Zyvex Performance Materials, using CNT technology in a number of their bicycle components—including flat and riser handlebars, cranks, forks, seatposts, stems and aero bars.
- Zyvex Technologies has also built a 54' maritime vessel, the Piranha Unmanned Surface Vessel, as a technology demonstrator for what is possible using CNT technology. CNTs help improve the structural performance of the vessel, resulting in a lightweight 8,000 lb boat that can carry a payload of 15,000 lb over a range of 2,500 miles.
- Amroy Europe Oy manufactures Hybtonite carbon nanoepoxy resins where carbon nanotubes have been chemically activated to bond to epoxy, resulting in a composite material that is 20% to 30% stronger than other composite materials. It has been used for wind turbines, marine paints and variety of sports gear such as skis, ice hockey sticks, baseball bats, hunting arrows, and surfboards.
Other current applications include:
- tips for atomic force microscope probes
- in tissue engineering, carbon nanotubes can act as scaffolding for bone growth
- See also, for last current applications: Timeline of carbon nanotubes
The strength and flexibility of carbon nanotubes makes them of potential use in controlling other nanoscale structures, which suggests they will have an important role in nanotechnology engineering. The highest tensile strength of an individual multi-walled carbon nanotube has been tested to be is 63 GPa. Carbon nanotubes were found in Damascus steel from the 17th century, possibly helping to account for the legendary strength of the swords made of it.
Because of the carbon nanotube's superior mechanical properties, many structures have been proposed ranging from everyday items like clothes and sports gear to combat jackets and space elevators. However, the space elevator will require further efforts in refining carbon nanotube technology, as the practical tensile strength of carbon nanotubes can still be greatly improved.
For perspective, outstanding breakthroughs have already been made. Pioneering work led by Ray H. Baughman at the NanoTech Institute has shown that single and multi-walled nanotubes can produce materials with toughness unmatched in the man-made and natural worlds.
Carbon nanotubes are also a promising material as building blocks in bio-mimetic hierarchical composite materials given their exceptional mechanical properties (~1TPa in modulus, and ~100 GPa in strength). Initial attempts to incorporate CNTs into hierarchical structures led to mechanical properties that were significantly lower than these achievable limits. Windle et al. have used an in situ chemical vapor deposition (CVD) spinning method to produce continuous CNT yarns from CVD grown CNT aerogels. With this technology, they fabricated CNT yarns with strengths as high as ~9 GPa at small gage lengths of ~1 mm, however, defects resulted in a reduction of specific strength to ~1 GPa at 20 mm gage length. Espinosa et al. developed high performance DWNT-polymer composite yarns by twisting and stretching ribbons of randomly oriented bundles of DWNTs thinly coated with polymeric organic compounds. These DWNT-polymer yarns exhibited unusually high energy to failure of ~100 J·g−1 (comparable to one of the toughest natural materials – spider silk), and strength as high as ~1.4 GPa. Effort is ongoing to produce CNT composites that incorporate tougher matrix materials, such as Kevlar, to further improve on the mechanical properties toward those of individual CNTs.
Because of the high mechanical strength of carbon nanotubes, research is being made into weaving them into clothes to create stab-proof and bulletproof clothing. The nanotubes would effectively stop the bullet from penetrating the body, although the bullet's kinetic energy would likely cause broken bones and internal bleeding.
In electrical circuits
Nanotube-based transistors, also known as carbon nanotube field-effect transistors (CNFETs), have been made that operate at room temperature and that are capable of digital switching using a single electron. However, one major obstacle to realization of nanotubes has been the lack of technology for mass production. In 2001 IBM researchers demonstrated how metallic nanotubes can be destroyed, leaving semiconducting ones behind for use as transistors. Their process is called "constructive destruction," which includes the automatic destruction of defective nanotubes on the wafer. This process, however, only gives control over the electrical properties on a statistical scale.
The potential of carbon nanotubes was demonstrated in 2003 when room-temperature ballistic transistors with ohmic metal contacts and high-k gate dielectric were reported, showing 20–30x higher ON current than state-of-the-art Si MOSFETs. This presented an important advance in the field as CNT was shown to potentially outperform Si. At the time, a major challenge was ohmic metal contact formation. In this regard, palladium, which is a high-work function metal was shown to exhibit Schottky barrier-free contacts to semiconducting nanotubes with diameters >1.7 nm.
The first nanotube integrated memory circuit was made in 2004. One of the main challenges has been regulating the conductivity of nanotubes. Depending on subtle surface features a nanotube may act as a plain conductor or as a semiconductor. A fully automated method has however been developed to remove non-semiconductor tubes.
Another way to make carbon nanotube transistors has been to use random networks of them. By doing so one averages all of their electrical differences and one can produce devices in large scale at the wafer level. This approach was first patented by Nanomix Inc.(date of original application June 2002 ). It was first published in the academic literature by the United States Naval Research Laboratory in 2003 through independent research work. This approach also enabled Nanomix to make the first transistor on a flexible and transparent substrate.
Large structures of carbon nanotubes can be used for thermal management of electronic circuits. An approximately 1 mm–thick carbon nanotube layer was used as a special material to fabricate coolers, this materials has very low density, ~20 times lower weight than a similar copper structure, while the cooling properties are similar for the two materials.
Overall, incorporating carbon nanotubes as transistors into logic-gate circuits with densities comparable to modern CMOS technology has not yet been demonstrated.
As electrical cables and wires
Wires for carrying electrical current may be fabricated from pure nanotubes and nanotube-polymer composites. Recently small wires have been fabricated with specific conductivity exceeding copper and aluminum; these cables are the highest conductivity carbon nanotube and also highest conductivity non-metal cables.
As paper batteries
A paper battery is a battery engineered to use a paper-thin sheet of cellulose (which is the major constituent of regular paper, among other things) infused with aligned carbon nanotubes. The nanotubes act as electrodes; allowing the storage devices to conduct electricity. The battery, which functions as both a lithium-ion battery and a supercapacitor, can provide a long, steady power output comparable to a conventional battery, as well as a supercapacitor’s quick burst of high energy—and while a conventional battery contains a number of separate components, the paper battery integrates all of the battery components in a single structure, making it more energy efficient.
Solar cells developed at the New Jersey Institute of Technology use a carbon nanotube complex, formed by a mixture of carbon nanotubes and carbon buckyballs (known as fullerenes) to form snake-like structures. Buckyballs trap electrons, although they can't make electrons flow. Add sunlight to excite the polymers, and the buckyballs will grab the electrons. Nanotubes, behaving like copper wires, will then be able to make the electrons or current flow.
MIT Laboratory for Electromagnetic and Electronic Systems uses nanotubes to improve ultracapacitors. The activated charcoal used in conventional ultracapacitors has many small hollow spaces of various size, which create together a large surface to store electric charge. But as charge is quantized into elementary charges, i.e. electrons, and each such elementary charge needs a minimum space, a significant fraction of the electrode surface is not available for storage because the hollow spaces are not compatible with the charge's requirements. With a nanotube electrode the spaces may be tailored to size—few too large or too small—and consequently the capacity should be increased considerably.
In the Kanzius cancer therapy, single-walled carbon nanotubes are inserted around cancerous cells, then excited with radio waves, which causes them to heat up and kill the surrounding cells.
Researchers at Rice University, Radboud University Nijmegen Medical Centre and University of California, Riverside have shown that carbon nanotubes and their polymer nanocomposites are suitable scaffold materials for bone cell proliferation  and bone formation.
Carbon nanotubes have been implemented in nanoelectromechanical systems, including mechanical memory elements (NRAM being developed by Nantero Inc.) and nanoscale electric motors (see Nanomotor or Nanotube nanomotor).
In May 2005, Nanomix Inc. placed on the market a hydrogen sensor that integrated carbon nanotubes on a silicon platform. Since then, Nanomix has been patenting many such sensor applications, such as in the field of carbon dioxide, nitrous oxide, glucose, DNA detection, etc.
Eikos Inc of Franklin, Massachusetts and Unidym Inc. of Silicon Valley, California are developing transparent, electrically conductive films of carbon nanotubes to replace indium tin oxide (ITO). Carbon nanotube films are substantially more mechanically robust than ITO films, making them ideal for high-reliability touchscreens and flexible displays. Printable water-based inks of carbon nanotubes are desired to enable the production of these films to replace ITO. Nanotube films show promise for use in displays for computers, cell phones, PDAs, and ATMs.
A nanoradio, a radio receiver consisting of a single nanotube, was demonstrated in 2007. In 2008 it was shown that a sheet of nanotubes can operate as a loudspeaker if an alternating current is applied. The sound is not produced through vibration but thermoacoustically.
A flywheel made of carbon nanotubes could be spun at extremely high velocity on a floating magnetic axis in a vacuum, and potentially store energy at a density approaching that of conventional fossil fuels. Since energy can be added to and removed from flywheels very efficiently in the form of electricity, this might offer a way of storing electricity, making the electrical grid more efficient and variable power suppliers (like wind turbines) more useful in meeting energy needs. The practicality of this depends heavily upon the cost of making massive, unbroken nanotube structures, and their failure rate under stress.
Carbon nanotube springs have the potential to indefinitely store elastic potential energy at ten times the density of lithium-ion batteries with flexible charge and discharge rates and extremely high cycling durability.
Ultra-short SWNTs (US-tubes) have been used as nanoscaled capsules for delivering MRI contrast agents in vivo.
Nitrogen-doped carbon nanotubes may replace platinum catalysts used to reduce oxygen in fuel cells. A forest of vertically-aligned nanotubes can reduce oxygen in alkaline solution more effectively than platinum, which has been used in such applications since the 1960s. The nanotubes have the added benefit of not being subject to carbon monoxide poisoning.
A 2006 editorial written by Marc Monthioux and Vladimir Kuznetsov in the journal Carbon described the interesting and often-misstated origin of the carbon nanotube. A large percentage of academic and popular literature attributes the discovery of hollow, nanometer-size tubes composed of graphitic carbon to Sumio Iijima of NEC in 1991.
In 1952 L. V. Radushkevich and V. M. Lukyanovich published clear images of 50 nanometer diameter tubes made of carbon in the Soviet Journal of Physical Chemistry. This discovery was largely unnoticed, as the article was published in the Russian language, and Western scientists' access to Soviet press was limited during the Cold War. It is likely that carbon nanotubes were produced before this date, but the invention of the transmission electron microscope (TEM) allowed direct visualization of these structures.
Carbon nanotubes have been produced and observed under a variety of conditions prior to 1991. A paper by Oberlin, Endo, and Koyama published in 1976 clearly showed hollow carbon fibers with nanometer-scale diameters using a vapor-growth technique. Additionally, the authors show a TEM image of a nanotube consisting of a single wall of graphene. Later, Endo has referred to this image as a single-walled nanotube.
In 1979, John Abrahamson presented evidence of carbon nanotubes at the 14th Biennial Conference of Carbon at Pennsylvania State University. The conference paper described carbon nanotubes as carbon fibers that were produced on carbon anodes during arc discharge. A characterization of these fibers was given as well as hypotheses for their growth in a nitrogen atmosphere at low pressures.
In 1981, a group of Soviet scientists published the results of chemical and structural characterization of carbon nanoparticles produced by a thermocatalytical disproportionation of carbon monoxide. Using TEM images and XRD patterns, the authors suggested that their “carbon multi-layer tubular crystals” were formed by rolling graphene layers into cylinders. They speculated that by rolling graphene layers into a cylinder, many different arrangements of graphene hexagonal nets are possible. They suggested two possibilities of such arrangements: circular arrangement (armchair nanotube) and a spiral, helical arrangement (chiral tube).
In 1987, Howard G. Tennett of Hyperion Catalysis was issued a U.S. patent for the production of "cylindrical discrete carbon fibrils" with a "constant diameter between about 3.5 and about 70 nanometers..., length 102 times the diameter, and an outer region of multiple essentially continuous layers of ordered carbon atoms and a distinct inner core...."
Iijima's discovery of multi-walled carbon nanotubes in the insoluble material of arc-burned graphite rods in 1991 and Mintmire, Dunlap, and White's independent prediction that if single-walled carbon nanotubes could be made, then they would exhibit remarkable conducting properties  helped create the initial buzz that is now associated with carbon nanotubes. Nanotube research accelerated greatly following the independent discoveries by Bethune at IBM and Iijima at NEC of single-walled carbon nanotubes and methods to specifically produce them by adding transition-metal catalysts to the carbon in an arc discharge. The arc discharge technique was well-known to produce the famed Buckminster fullerene on a preparative scale, and these results appeared to extend the run of accidental discoveries relating to fullerenes. The original observation of fullerenes in mass spectrometry was not anticipated, and the first mass-production technique by Krätschmer and Huffman was used for several years before realizing that it produced fullerenes.
The discovery of nanotubes remains a contentious issue. Many believe that Iijima's report in 1991 is of particular importance because it brought carbon nanotubes into the awareness of the scientific community as a whole.
- Allotropes of carbon
- Boron nitride nanotube
- Carbon nanotubes in photovoltaics
- Graphene oxide paper
- Carbon nanotube chemistry
- List of software for nanostructures modeling
- Optical properties of carbon nanotubes
- Organic electronics
- Selective chemistry of single-walled nanotubes
- Potential applications of carbon nanotubes
- Colossal carbon tube
- Molecular modeling
- Silicon nanotubes
- Tunable nanoporous carbon
- Carbon nanoparticles
- Carbon nanofibers
- Carbon nanocone
- Nanotube modelling software -Ninithi
- ^ a b Wang, X. et al. (2009). "Fabrication of Ultralong and Electrically Uniform Single-Walled Carbon Nanotubes on Clean Substrates". Nano Letters 9 (9): 3137–3141. Bibcode 2009NanoL...9.3137W. doi:10.1021/nl901260b. PMID 19650638.
- ^ Martel, R. et al. (2001). "Ambipolar Electrical Transport in Semiconducting Single-Wall Carbon Nanotubes". Physical Review Letters 87 (25): 256805. Bibcode 2001PhRvL..87y6805M. doi:10.1103/PhysRevLett.87.256805. PMID 11736597.
- ^ "Carbon Solutions, Inc.". http://www.carbonsolution.com.
- ^ "CarboLex". http://carbolex.com.
- ^ Flahaut, E.; Bacsa, R; Peigney, A; Laurent, C (2003). "Gram-Scale CCVD Synthesis of Double-Walled Carbon Nanotubes". Chemical Communications 12 (12): 1442–1443. doi:10.1039/b301514a. PMID 12841282.
- ^ Cumings, John; Zettl, A. (2000). "Low-Friction Nanoscale Linear Bearing Realized from Multiwall Carbon Nanotubes". Science 289 (5479): 602–604. Bibcode 2000Sci...289..602C. doi:10.1126/science.289.5479.602. PMID 10915618.
- ^ Treacy, M.M.J.; Ebbesen, T.W.; Gibson, J.M. (1996). "Exceptionally high Young's modulus observed for individual carbon nanotubes". Nature 381 (6584): 678–680. Bibcode 1996Natur.381..678T. doi:10.1038/381678a0.
- ^ Zavalniuk, Vladimir; Marchenko, Sergey (2011). "Theoretical analysis of telescopic oscillations in multi-walled carbon nanotubes". Low Temp. Phys. 37 (4): 337 (6 pages). Bibcode 2011LTP....37..337Z. doi:10.1063/1.3592692.
- ^ a b Liu, Lei; Guo, G. Y.; Jayanthi, C. S.; Wu, S. Y. (2002). "Colossal Paramagnetic Moments in Metallic Carbon Nanotori". Physical Review Letters 88 (21): 217206. Bibcode 2002PhRvL..88u7206L. doi:10.1103/PhysRevLett.88.217206. PMID 12059501.
- ^ Huhtala, Maria (2002). "Carbon nanotube structures: molecular dynamics simulation at realistic limit" (PDF). Computer Physics Communications 146: 30. Bibcode 2002CoPhC.146...30H. doi:10.1016/S0010-4655(02)00432-0. http://www.princeton.edu/~msammalk/publications/cpc146_02.pdf.
- ^ Liu, Q. et al., Qingfeng; Ren, Wencai; Chen, Zhi-Gang; Yin, Lichang; Li, Feng; Cong, Hongtao; Cheng, Hui-Ming (2009). "Semiconducting properties of cup-stacked carbon nanotubes". Carbon 47 (3): 731–736. doi:10.1016/j.carbon.2008.11.005. http://carbon.imr.ac.cn/file/Journal/2009/1249016438117.pdf.
- ^ "A Better Way to Make Nanotubes". Berkeley Lab.. January 5, 2009. http://newscenter.lbl.gov/feature-stories/2009/01/05/better-way-to-make-nanotubes/.
- ^ "Carbon Nanohoops: Shortest Segment of a Carbon Nanotube Synthesized". Berkeley Lab.. http://www.lbl.gov/msd/assets/docs/highlights/09-Bertozzi.pdf.
- ^ "Synthetic organic chemistry". A centre of chemistry excellence. Nature. October 7, 2009. http://www.nature.com/naturejobs/2009/091008/full/nj0264.html#a-centre-of-chemistry-excellence.
- ^ Zhao, X.; Liu, Y.; Inoue, S.; Suzuki, T.; Jones, R. O.; Andol, Y. (2004). "Smallest Carbon Nanotube is 3 Å in Diameter". Physical Review Letters 92 (12): 125502. Bibcode 2004PhRvL..92l5502Z. doi:10.1103/PhysRevLett.92.125502. PMID 15089683.
- ^ Hayashi, Takuya et al. (2003). "Smallest Freestanding Single-Walled Carbon Nanotube". Nano Letters 3 (7): 887–889. Bibcode 2003NanoL...3..887H. doi:10.1021/nl034080r.
- ^ Guan, Lunhui; Suenaga, Kazu; Iijima, Sumio (2008). "Smallest Carbon Nanotube Assigned with Atomic Resolution Accuracy". Nano Letters 8 (2): 459–462. Bibcode 2008NanoL...8..459G. doi:10.1021/nl072396j. PMID 18186659.
- ^ a b c d e f Yu, Min-Feng; Lourie, Oleg; Dyer, Mark J.; Moloni, Katerina; Kelly, Thomas F.; Ruoff, Rodney S. (28 January 2000). "Strength and Breaking Mechanism of Multiwalled Carbon Nanotubes Under Tensile Load". Science 287 (5453): 637–640. Bibcode 2000Sci...287..637Y. doi:10.1126/science.287.5453.637. PMID 10649994.
- ^ a b B. Peng, M. Locascio, P. Zapol, S. Li, S. L. Mielke, G. C. Schatz, and H. D. Espinosa, "Measurements of near-ultimate strength for multiwalled carbon nanotubes and irradiation-induced crosslinking improvements," Nature Nanotechnology, vol. 3, pp. 626 – 631, 2008.
- ^ a b c d Collins, Philip G. (2000). "Nanotubes for Electronics" (PDF). Scientific American: 67–69. http://www.crhc.uiuc.edu/ece497nc/fall01/papers/NTs_SciAm_2000.pdf.
- ^ a b T. Filleter, R. A. Berrnal, S. Li, and H. D. Espinosa, "Ultrahigh Strength and Stiffness in Cross-Linked Hierarchical Carbon Nanotube Bundles," Adv. Mater., (in press), 2011.
- ^ K. Jensen, W. Mickelson, A. Kis, and A. Zettl. Buckling and kinking force measurements on individual multiwalled carbon nanotubes. Phys. Rev. B 76, 195436 (2007)
- ^ Belluci, S. (19 January 2005). "Carbon nanotubes: physics and applications". Physica Status Solidi (c) 2 (1): 34–47. Bibcode 2005PSSCR...2...34B. doi:10.1002/pssc.200460105.
- ^ Chae, Han Gi; Kumar, Satish (26 January 2006). "Rigid Rod Polymeric Fibers". Journal of Applied Polymer Science 100 (1): 791–802. doi:10.1002/app.22680.
- ^ Meo, Michele; Rossi, Marco (3 February 2006). "Prediction of Young's modulus of single wall carbon nanotubes by molecular-mechanics-based ﬁnite element modelling". Composites Science and Technology 66 (11–12): 1597–1605. doi:10.1016/j.compscitech.2005.11.015.
- ^ Sinnott, Susan B.; Andrews, Rodney (July 2001). "Carbon Nanotubes: Synthesis, Properties, and Applications". Critical Reviews in Solid State and Materials Sciences 26 (3): 145–249. doi:10.1080/20014091104189.
- ^ a b Demczyk, B.G.; Wang, Y; Cumings, J; Hetman, M; Han, W; Zettl, A; Ritchie, R (2002). "Direct mechanical measurement of the tensile strength and elastic modulus of multiwalled carbon nanotubes". Materials Science and Engineering A 334 (1–2): 173–178. doi:10.1016/S0921-5093(01)01807-X.
- ^ a b Australian Stainless Steel Development Association (ASSDA) – Properties of Stainless Steel
- ^ a b Stainless Steel – 17-7PH (Fe/Cr17/Ni 7) Material Information
- ^ a b H. D. Wagner (2002). "Reinforcement". Encyclopedia of Polymer Science and Technology. John Wiley & Sons. doi:10.1002/0471440264.pst317. http://www.weizmann.ac.il/wagner/COURSES/Reading%20material%20(papers)/Encyclopedy_of_polymer_science_2003.pdf.
- ^ R. S. Ruoff, et al., "Radial deformation of carbon nanotubes by van der Waals forces" Nature 364, 514 (1993)
- ^ I. Palaci, et al. "Radial Elasticity of Multiwalled Carbon Nanotubes" Phys. Rev. Lett. 94, 175502 (2005)
- ^ M.-F. Yu, et al. "Investigation of the Radial Deformability of Individual Carbon Nanotubes under Controlled Indentation Force" Phys. Rev. Lett. 85, 1456–1459 (2000)
- ^ Y.H.Yang et al. (2011). "Radial elasticity of single-walled carbon nanotube measured by atomic force microscopy". Applied Physics Letters 98: 041901. doi:10.1063/ApplPhysLett.98.041901.
- ^ M. Popov et al. (2002). "Superhard phase composed of single-wall carbon nanotubes". Phys. Rev. B 65 (3): 033408. Bibcode 2002PhRvB..65c3408P. doi:10.1103/PhysRevB.65.033408. http://www.ssl.physics.ncsu.edu/publication/browse/getFileAction?fileref=2003-02-27+12:53:01&dbfilename=2002-PRB65-033408.pdf.
- ^ 07.23.2003 – Physicists build world's smallest motor using nanotubes and etched silicon
- ^ a b Lu, X.; Chen, Z. (2005). "Curved Pi-Conjugation, Aromaticity, and the Related Chemistry of Small Fullerenes (<C60) and Single-Walled Carbon Nanotubes". Chemical Reviews 105 (10): 3643–3696. doi:10.1021/cr030093d. PMID 16218563.
- ^ Hong, Seunghun; Myung, S (2007). "Nanotube Electronics: A flexible approach to mobility". Nature Nanotechnology 2 (4): 207–208. Bibcode 2007NatNa...2..207H. doi:10.1038/nnano.2007.89. PMID 18654263.
- ^ J. Haruyama et al. (2006). "Superconductivity in Entirely End-Bonded Multiwalled Carbon Nanotubes". Physical Review Letters 96 (5): 057001. arXiv:cond-mat/0509466. Bibcode 2006PhRvL..96e7001T. doi:10.1103/PhysRevLett.96.057001. PMID 16486971. http://www.ee.aoyama.ac.jp/Labs/j-haru-www/paper/Haruyama%20SuperCNT%20PRL%20publication.pdf.
- ^ Pop, Eric et al.; Mann, David; Wang, Qian; Goodson, Kenneth; Dai, Hongjie (2005-12-22). "Thermal conductance of an individual single-wall carbon nanotube above room temperature". Nano Letters 6 (1): 96–100. arXiv:cond-mat/0512624. Bibcode 2006NanoL...6...96P. doi:10.1021/nl052145f. PMID 16402794.
- ^ Sinha, Saion et al.; Barjami, Saimir; Iannacchione, Germano; Schwab, Alexander; Muench, George (2005-06-05). "Off-axis thermal properties of carbon nanotube films". Journal of Nanoparticle Research 7 (6): 651–657. doi:10.1007/s11051-005-8382-9.
- ^ Thostenson, Erik; Li, C; Chou, T (2005). "Nanocomposites in context". Composites Science and Technology 65 (3–4): 491–516. doi:10.1016/j.compscitech.2004.11.003.
- ^ Carbon-Based Magnetism: An Overview of the Magnetism of Metal Free Carbon-based Compounds and Materials, edited by Tatiana Makarova and Fernando Palacio (Elsevier 2006)
- ^ Mingo, N.; Stewart, D. A.; Broido, D. A.; Srivastava, D. (2008). "Phonon transmission through defects in carbon nanotubes from first principles". Physical Review B 77 (3): 033418. Bibcode 2008PhRvB..77c3418M. doi:10.1103/PhysRevB.77.033418.
- ^ a b Kolosnjaj J, Szwarc H, Moussa F (2007). "Toxicity studies of carbon nanotubes". Adv Exp Med Biol.. Advances in Experimental Medicine and Biology 620: 181–204. doi:10.1007/978-0-387-76713-0_14. ISBN 978-0-387-76712-3. PMID 18217344.
- ^ a b Porter, Alexandra; Gass, Mhairi; Muller, Karin; Skepper, Jeremy N.; Midgley, Paul A.; Welland, Mark (2007). "Direct imaging of single-walled carbon nanotubes in cells". Nature Nanotechnology 2 (11): 713. Bibcode 2007NatNa...2..713P. doi:10.1038/nnano.2007.347. PMID 18654411.
- ^ Zumwalde, Ralph and Laura Hodson (March 2009). "Approaches to Safe Nanotechnology: Managing the Health and Safety Concerns Associated with Engineered Nanomaterials". National Institute for Occupational Safety and Health. NIOSH (DHHS) Publication 2009-125.
- ^ a b Lam CW, James JT, McCluskey R, Arepalli S, Hunter RL (2006). "A review of carbon nanotube toxicity and assessment of potential occupational and environmental health risks". Crit Rev Toxicol. 36 (3): 189–217. doi:10.1080/10408440600570233. PMID 16686422.
- ^ a b c Poland, CA; Duffin, Rodger; Kinloch, Ian; Maynard, Andrew; Wallace, William A. H.; Seaton, Anthony; Stone, Vicki; Brown, Simon et al. (2008). "Carbon nanotubes introduced into the abdominal cavity of mice show asbestos-like pathogenicity in a pilot study". Nature Nanotechnology 3 (7): 423. doi:10.1038/nnano.2008.111. PMID 18654567.
- ^ Carbon Nanotubes That Look Like Asbestos, Behave Like Asbestos
- ^ Iijima, Sumio (1991). "Helical microtubules of graphitic carbon". Nature 354 (6348): 56–58. Bibcode 1991Natur.354...56I. doi:10.1038/354056a0.
- ^ Ebbesen, T. W.; Ajayan, P. M. (1992). "Large-scale synthesis of carbon nanotubes". Nature 358 (6383): 220–222. Bibcode 1992Natur.358..220E. doi:10.1038/358220a0.
- ^ Guo, Ting; Nikolaev, Pavel; Rinzler, Andrew G.; Tomanek, David; Colbert, Daniel T.; Smalley, Richard E. (1995). "Self-Assembly of Tubular Fullerenes". J. Phys. Chem. 99 (27): 10694–10697. doi:10.1021/j100027a002. http://www.pa.msu.edu/cmp/csc/eprint/DT085.pdf.
- ^ Guo, Ting; Nikolaev, P; Thess, A; Colbert, D; Smalley, R (1995). "Catalytic growth of single-walled nanotubes by laser vaporization" (PDF). Chem. Phys. Lett. 243: 49–54. Bibcode 1995CPL...243...49B. doi:10.1016/0009-2614(95)00825-O. http://www.orgchem.science.ru.nl/molmat/mm-web/education/caput-college/ChemPhysLett-1995-243-49.pdf.
- ^ Walker Jr., P. L.; Rakszawski, J. F.; Imperial, G. R. (1959). "Carbon Formation from Carbon Monoxide-Hydrogen Mixtures over Iron Catalysts. I. Properties of Carbon Formed". J. Phys. Chem. 63 (2): 133. doi:10.1021/j150572a002.
- ^ José-Yacamán, M.; Miki-Yoshida, M.; Rendón, L.; Santiesteban, J. G. (1993). "Catalytic growth of carbon microtubules with fullerene structure". Appl. Phys. Lett. 62 (6): 657. Bibcode 1993ApPhL..62..657J. doi:10.1063/1.108857.
- ^ Beckman, Wendy (2007-04-27). "UC Researchers Shatter World Records with Length of Carbon Nanotube Arrays". University of Cincinnati. http://www.uc.edu/news/NR.asp?id=5700.
- ^ N. Inami et al. "Synthesis-condition dependence of carbon nanotube growth by alcohol catalytic chemical vapor deposition method" Sci. Technol. Adv. Mater. 8 (2007) 292 free download
- ^ N. Ishigami; Ago, H; Imamoto, K; Tsuji, M; Iakoubovskii, K; Minami, N (2008). "Crystal Plane Dependent Growth of Aligned Single-Walled Carbon Nanotubes on Sapphire". J. Am. Chem. Soc. 130 (30): 9918–9924. doi:10.1021/ja8024752. PMID 18597459.
- ^ Pinilla, JL; Moliner, R; Suelves, I; Lazaro, M; Echegoyen, Y; Palacios, J (2007). "Production of hydrogen and carbon nanofibers by thermal decomposition of methane using metal catalysts in a fluidized bed reactor". International Journal of Hydrogen Energy 32 (18): 4821. doi:10.1016/j.ijhydene.2007.08.013.
- ^ Muradov, N (2001). "Hydrogen via methane decomposition: an application for decarbonization of fossil fuels". International Journal of Hydrogen Energy 26 (11): 1165–1175. doi:10.1016/S0360-3199(01)00073-8.
- ^ Eftekhari, A.; Jafarkhani, P; Moztarzadeh, F (2006). "High-yield synthesis of carbon nanotubes using a water-soluble catalyst support in catalytic chemical vapor deposition". Carbon 44 (7): 1343. doi:10.1016/j.carbon.2005.12.006.
- ^ Ren, Z. F. et al. (1998). "Synthesis of Large Arrays of Well-Aligned Carbon Nanotubes on Glass". Science 282 (5391): 1105. Bibcode 1998Sci...282.1105R. doi:10.1126/science.282.5391.1105. PMID 9804545.
- ^ SEM images & TEM images of carbon nanotubes, aligned carbon nanotube arrays, and nanoparticles
- ^ Kumar, Mukul; Ando, Yoshinori (2007). "Carbon Nanotubes from Camphor: An Environment-Friendly Nanotechnology". Journal of Physics: Conference Series 61: 643. Bibcode 2007JPhCS..61..643K. doi:10.1088/1742-6596/61/1/129. http://www.iop.org/EJ/article/1742-6596/61/1/129/jpconf7_61_129.pdf.
- ^ Boyd, Jade (2006-11-17). "Rice chemists create, grow nanotube seeds". Rice University. http://www.media.rice.edu/media/NewsBot.asp?MODE=VIEW&ID=9070.
- ^ K. Hata et al. (2004). "Water-Assisted Highly Efficient Synthesis of Impurity-Free Single-Walled Carbon Nanotubes". Science 306 (5700): 1362–1365. Bibcode 2004Sci...306.1362H. doi:10.1126/science.1104962. PMID 15550668.
- ^ K. Hata et al. (2005). "Kinetics of Water-Assisted Single-Walled Carbon Nanotube Synthesis Revealed by a Time-Evolution Analysis". Physical Review Letters 95 (5): 056104. Bibcode 2005PhRvL..95e6104F. doi:10.1103/PhysRevLett.95.056104.
- ^ K. Hata, Sumio Iijima et al. (2009). "Compact and light supercapacitors from a surface-only solid by opened carbon nanotubes with 2,200 m2/g". Advanced Functional Materials 20 (3): 422–428. doi:10.1002/adfm.200901927.
- ^ "Unidym product sheet SWNT". http://www.unidym.com/files/Unidym_Product_Sheet_SWNT.pdf.
- ^ "Characteristic of Carbon nanotubes by super-growth method" (in japanese). http://www.nanocarbon.jp/sg/002.html.
- ^ a b K.Hata. "From Highly Efficient Impurity-Free CNT Synthesis to DWNT forests, CNTsolids and Super-Capacitors". http://www.nanocarbon.jp/english/research/image/review.pdf.
- ^ Takeo Yamada et al. (2006). "Size-selective growth of double-walled carbon nanotube forests from engineered iron catalysts". Nature Nanotechnology 1 (2): 131–136. Bibcode 2006NatNa...1..131Y. doi:10.1038/nnano.2006.95. PMID 18654165.
- ^ Don N. Futaba , Kenji Hata et al. (2006). "Shape-engineerable and highly densely packed single-walled carbon nanotubes and their application as super-capacitor electrodes". Nature Materials 5 (12): 987–994. Bibcode 2006NatMa...5..987F. doi:10.1038/nmat1782. PMID 17128258.
- ^ Singer, J.M. (1959). "Carbon formation in very rich hydrocarbon-air flames. I. Studies of chemical content, temperature, ionization and particulate matter". Seventh Symposium (International) on Combustion.
- ^ Yuan, Liming (2001). "Nanotubes from methane flames". Chemical physics letters 340 (3–4): 237–241. Bibcode 2001CPL...340..237Y. doi:10.1016/S0009-2614(01)00435-3.
- ^ Yuan, Liming (2001). "Ethylene flame synthesis of well-aligned multi-walled carbon nanotubes". Chemical physics letters 346: 23–28. Bibcode 2001CPL...346...23Y. doi:10.1016/S0009-2614(01)00959-9.
- ^ Duan, H. M.; McKinnon, J. T. (1994). "Nanoclusters Produced in Flames". Journal of Physical Chemistry 98 (49): 12815–12818. doi:10.1021/j100100a001.
- ^ Murr, L. E.; Bang, J.J.; Esquivel, E.V.; Guerrero, P.A.; Lopez, D.A. (2004). "Carbon nanotubes, nanocrystal forms, and complex nanoparticle aggregates in common fuel-gas combustion sources and the ambient air". Journal of Nanoparticle Research 6 (2/3): 241–251. doi:10.1023/B:NANO.0000034651.91325.40.
- ^ Vander Wal, R.L. (2002). "Fe-catalyzed single-walled carbon nanotube synthesis within a flame environment". Combust. Flame 130: 37–47. doi:10.1016/S0010-2180(02)00360-7.
- ^ Saveliev, A.V. (2003). "Metal catalyzed synthesis of carbon nanostructures in an opposed flow methane oxygen flame". Combust. Flame 135: 27–33. doi:10.1016/S0010-2180(03)00142-1.
- ^ Height, M.J. (2004). "Flame synthesis of single-walled carbon nanotubes". Carbon 42 (11): 2295–2307. doi:10.1016/j.carbon.2004.05.010.
- ^ Sen, S.; Puri, Ishwar K (2004). "Flame synthesis of carbon nanofibers and nanofibers composites containing encapsulated metal particles". Nanotechnology 15 (3): 264–268. Bibcode 2004Nanot..15..264S. doi:10.1088/0957-4484/15/3/005.
- ^ a b Arnold, Michael S.; Green, Alexander A.; Hulvat, James F.; Stupp, Samuel I.; Hersam, Mark C. (2006). "Sorting carbon nanotubes by electronic structure using density differentiation". Nature Nanotechnology 1 (1): 60–5. Bibcode 2006NatNa...1...60A. doi:10.1038/nnano.2006.52. PMID 18654143.
- ^ Takeshi Tanaka et al. (2009). "Simple and Scalable Gel-Based Separation of Metallic and Semiconducting Carbon Nanotubes". Nano Letters 9 (4): 1497–1500. Bibcode 2009NanoL...9.1497T. doi:10.1021/nl8034866. PMID 19243112.
- ^ T.Tanaka. "New, Simple Method for Separation of Metallic and Semiconducting Carbon Nanotubes". http://www.aist.go.jp/aist_e/latest_research/2009/20090406/20090406.html.
- ^ Takeshi Tanaka et al. (2009). "Continuous Separation of Metallic and Semiconducting Carbon Nanotubes Using Agarose Gel". Applied Physics Express 2 (12): 125002. Bibcode 2009APExp...2l5002T. doi:10.1143/APEX.2.125002.
- ^ Huang, X et al. (2005). "High-Resolution Length Sorting and Purification of DNA-Wrapped Carbon Nanotubes by Size-Exclusion Chromatography". Anal. Chem. 77 (19): 6225–6228. doi:10.1021/ac0508954. PMID 16194082.
- ^ Mark C Hersam (2008). "Progress towards monodisperse single-walled carbon nanotubes". Nature Nanotechnology 3 (7): 387–394. Bibcode 2008NatNa...3..387H. doi:10.1038/nnano.2008.135. PMID 18654561.
- ^ Zheng, M et al. (2003). "Structure-Based Carbon Nanotube Sorting by Sequence-Dependent DNA Assembly". Science 302 (5650): 1545–1548. Bibcode 2003Sci...302.1545Z. doi:10.1126/science.1091911. PMID 14645843.
- ^ Tu, Helen et al. (2009). "DNA sequence motifs for structure-specific recognition and separation of carbon nanotubes". Nature 460 (7252): 250–253. Bibcode 2009Natur.460..250T. doi:10.1038/nature08116. PMID 19587767.
- ^ Zhang, L et al. (2009). "Optical characterizations and electronic devices of nearly pure (10,5) single-walled carbon nanotubes". J Am Chem Soc 131 (7): 2454–2455. doi:10.1021/ja8096674. PMID 19193007.
- ^ Ding, Lei et al. (2009). "Selective Growth of Well-Aligned Semiconducting Single-Walled Carbon Nanotubes". Nano Letters 9 (2): 800–5. Bibcode 2009NanoL...9..800D. doi:10.1021/nl803496s. PMID 19159186.
- ^ M.A. Mohamed; Ambri Mohamed, Mohd; Shikoh, Eiji; Fujiwara, Akihiko (2007). "Fabrication of spintronics device by direct synthesis of single-walled carbon nanotubes from ferromagnetic electrodes". Sci. Technol. Adv. Mater. 8 (4): 292. Bibcode 2007STAdM...8..292I. doi:10.1016/j.stam.2007.02.009.
- ^ "Pirahna USV built using nano-enhanced carbon prepreg". ReinforcedPlastics.com. 19 February December 2009. http://www.reinforcedplastics.com/view/7467/pirahna-usv-built-using-nanoenhanced-carbon-prepreg/. Retrieved 25 February 2010.
- ^ Pagni, John (5 March 2010). "Amroy aims to become nano-leader". European Plastics News. http://www.europeanplasticsnews.com/subscriber/headlines2.html?cat=1&id=1267781513. Retrieved 2010-11-21.
- ^ "Nanotube Tips". nanoScince instruments. http://www.nanoscience.com/store/pc/viewCategories.asp?idCategory=9.
- ^ Zanello, Laura P.; Bin Zhao, Hui Hu, Robert C. Haddon (16). "Bone Cell Proliferation on Carbon Nanotubes". Nano Letters. 3 6 (3): 562–567. Bibcode 2006NanoL...6..562Z. doi:10.1021/nl051861e. PMID 16522063. http://pubs.acs.org/doi/abs/10.1021/nl051861e#nl051861eAF2. Retrieved 14 December 2010.
- ^ K. Sanderson (2006). "Sharpest cut from nanotube sword". Nature 444: 286. doi:10.1038/news061113-11.
- ^ Reibold, M.; Paufler, P; Levin, AA; Kochmann, W; Pätzke, N; Meyer, DC (November 16, 2006). "Materials:Carbon nanotubes in an ancient Damascus sabre". Nature 444 (7117): 286. Bibcode 2006Natur.444..286R. doi:10.1038/444286a. PMID 17108950.
- ^ Edwards, Brad C. (2003). The Space Elevator. BC Edwards. ISBN 0974651710.
- ^ Zhang, Mei et al. (2005). "Strong, Transparent, Multifunctional, Carbon Nanotube Sheets". Science 309 (5738): 1215–1219. Bibcode 2005Sci...309.1215Z. doi:10.1126/science.1115311. PMID 16109875.
- ^ Dalton, Alan B. et al. (2003). "Super-tough carbon-nanotube fibres". Nature 423 (4): 703. Bibcode 2003Natur.423..703D. doi:10.1038/423703a. PMID 18297073.
- ^ Miaudet, P. et al. (2005). "Hot-Drawing of Single and Multiwall Carbon Nanotube Fibers for High Toughness and Alignment". Nano Letters 5 (11): 2212–2215. Bibcode 2005NanoL...5.2212M. doi:10.1021/nl051419w. PMID 16277455.
- ^ Li, Y.-L. et al. (2004). "Direct Spinning of Carbon Nanotube Fibers from Chemical Vapor Deposition Synthesis". Science 304 (5668): 276–278. Bibcode 2004Sci...304..276L. doi:10.1126/science.1094982. PMID 15016960.
- ^ a b Motta, M. et al. (2007). "High Performance Fibres from 'Dog Bone' Carbon Nanotubes". Advanced Materials 19 (21): 3721–3726. doi:10.1002/adma.200700516.
- ^ Koziol, K. et al. (2007). "High-Performance Carbon Nanotube Fiber". Science 318 (5858): 1892–1895. Bibcode 2007Sci...318.1892K. doi:10.1126/science.1147635. PMID 18006708.
- ^ Yang, Y. et al. (2005). "Toughness of Spider Silk at High and Low Temperatures". Advanced Materials 17: 84–88. doi:10.1002/adma.200400344.
- ^ Naraghi, M. et al. (2010). "A Multiscale Study of High Performance Double-Walled Nanotube−Polymer Fibers". ACS Nano 4 (11): 6463–6476. doi:10.1021/nn101404u. PMID 20977259.
- ^ Yildirim, T.; Gülseren, O.; Kılıç, Ç.; Ciraci, S. (2000). "Pressure-induced interlinking of carbon nanotubes". Physical Review B 62 (19): 19. arXiv:cond-mat/0008476. Bibcode 2000PhRvB..6212648Y. doi:10.1103/PhysRevB.62.12648.
- ^ Postma, Henk W. Ch.; Teepen, T; Yao, Z; Grifoni, M; Dekker, C (2001). "Carbon Nanotube Single-Electron Transistors at Room temperature". Science 293 (5527): 76. Bibcode 2001Sci...293...76P. doi:10.1126/science.1061797. PMID 11441175.
- ^ Collins, Philip G.; Arnold, MS; Avouris, P (2001). "Engineering Carbon Nanotubes and Nanotube Circuits Using Electrical Breakdown". Science 292 (5517): 706–709. Bibcode 2001Sci...292..706C. doi:10.1126/science.1058782. PMID 11326094.
- ^ Javey, Ali; Guo, J; Wang, Q; Lundstrom, M; Dai, H (2003). "Ballistic Carbon Nanotube Transistors". Nature 424 (6949): 654–657. Bibcode 2003Natur.424..654J. doi:10.1038/nature01797. PMID 12904787.
- ^ Javey, A et al. (2004). "Self-aligned ballistic molecular transistors and electrically parallel nanotube arrays". Nano Letters 4 (7): 1319–1322. arXiv:cond-mat/0406494. Bibcode 2004NanoL...4.1319J. doi:10.1021/nl049222b.
- ^ Tseng, Yu-Chih et al. (2004). "Monolithic Integration of Carbon Nanotube Devices with Silicon MOS Technology". Nano Letters 4: 123–127. Bibcode 2004NanoL...4..123T. doi:10.1021/nl0349707.
- ^ Gabriel, Jean-Christophe P. (2003). "Large Scale Production of Carbon Nanotube Transistors: A Generic Platforms for Chemical Sensors". Mat. Res. Soc. Symp. Proc. 762: Q.12.7.1. http://www.mrs.org/s_mrs/sec_subscribe.asp?CID=2606&DID=110422&action=detail.
- ^ Nanōmix – Breakthrough Detection Solutions with the Nanoelectronic Sensation Technology
- ^ Gabriel, Jean-Christophe P.. "Dispersed Growth Of Nanotubes on a substrate". Patent WO 2004040671A2. http://www.freepatentsonline.com/EP1560958.html.
- ^ Bradley, Keith; Gabriel, Jean-Christophe P.; Grüner, George (2003). "Flexible nanotube transistors". Nano Letters 3 (10): 1353–1355. Bibcode 2003NanoL...3.1353B. doi:10.1021/nl0344864.
- ^ Armitage, Peter N.. "Flexible nanostructure electronic devices". United States Patent 20050184641 A1. http://www.freshpatents.com/Flexible-nanostructure-electronic-devices-dt20050825ptan20050184641.php. [dead link]
- ^ Kordas, K. et al. (2007). "Chip cooling with integrated carbon nanotube microfin architectures". Appl. Phys. Lett. 90 (12): 123105. Bibcode 2007ApPhL..90l3105K. doi:10.1063/1.2714281.
- ^ "Nanocables light way to the future". Youtube. September 09, 2011. http://www.youtube.com/watch?v=oJw6JmZmdqE.
- ^ Iodine doped carbon nanotube cables exceeding specific electrical conductivity of metals, Scientific Reports, Nature Publishing Group, September 06, 2011, http://www.nature.com/srep/2011/110906/srep00083/full/srep00083.html
- ^ "Beyond Batteries: Storing Power in a Sheet of Paper". Eurekalert.org. August 13, 2007. http://www.eurekalert.org/pub_releases/2007-08/rpi-bbs080907.php. Retrieved 2008-09-15.
- ^ "New Flexible Plastic Solar Panels Are Inexpensive And Easy To Make". ScienceDaily. July 19, 2007. http://www.sciencedaily.com/releases/2007/07/070719011151.htm.
- ^ MIT LEES on Batteries. MIT press release, 2006.
- ^ Haddon, Robert C.; Laura P. Zanello, Bin Zhao, Hui Hu (16). "Bone Cell Proliferation on Carbon Nanotubes". Nano Letters 6 (3): 562–567. Bibcode 2006NanoL...6..562Z. doi:10.1021/nl051861e. PMID 16522063.
- ^ Shi, Xinfeng et al. (2007). "Fabrication of porous ultra-short single-walled carbon nanotubenanocomposite scaffolds for bone tissue engineering". Biomaterials 28 (28): 4078–4090. doi:10.1016/j.biomaterials.2007.05.033. PMID 17576009.
- ^ Sitharaman, B. et al. (2008). "In vivo biocompatibility of ultra-short single-walled carbon nanotube/biodegradable polymer nanocomposites for bone tissue engineering". Bone 43 (2): 362–370. doi:10.1016/j.bone.2008.04.013. PMID 18541467.
- ^ Nanotubes May Heal Broken Bones
- ^ Simmons, Trevor; Hashim, D; Vajtai, R; Ajayan, PM (2007). "Large Area-Aligned Arrays from Direct Deposition of Single-Wall Carbon Nanotubes". J. Am. Chem. Soc. 129 (33): 10088–10089. doi:10.1021/ja073745e. PMID 17663555.
- ^ Hot nanotube sheets produce music on demand, New Scientists News, 31 October 2008
- ^ Nanotechnology and MRI contrast enhancement, Future Medicinal Chemistry March 2010, Vol. 2, No. 3, Pages 491–502
- ^ Chemical & Engineering News, 9 February 2009, "Nanotube Catalysts", p. 7
- ^ a b Monthioux, Marc; Kuznetsov, V (2006). "Who should be given the credit for the discovery of carbon nanotubes?" (PDF). Carbon 44 (9): 1621. doi:10.1016/j.carbon.2006.03.019. http://www.cemes.fr/fichpdf/GuestEditorial.pdf.
- ^ Радушкевич, Л. В. (1952). "О Структуре Углерода, Образующегося При Термическом Разложении Окиси Углерода На Железном Контакте" (in Russian) (PDF). Журнал Физической Химии 26: 88–95. http://carbon.phys.msu.ru/publications/1952-radushkevich-lukyanovich.pdf. (dead link)
- ^ Oberlin, A. (1976). "Filamentous growth of carbon through benzene decomposition". Journal of Crystal Growth 32 (3): 335–349. Bibcode 1976JCrGr..32..335O. doi:10.1016/0022-0248(76)90115-9.
- ^ Endo, Morinobu; Dresselhaus, M. S. (October 26, 2002). "Carbon Fibers and Carbon Nanotubes (Interview, Nagano, Japan)" (PDF). http://web.mit.edu/tinytech/Nanostructures/Spring2003/MDresselhaus/i789.pdf.
- ^ Abrahamson, John; Wiles, Peter G.; Rhoades, Brian L. (1999). "Structure of Carbon Fibers Found on Carbon Arc Anodes". Carbon 37 (11): 1873. doi:10.1016/S0008-6223(99)00199-2.
- ^ Izvestiya Akademii Nauk SSSR, Metals. 1982, #3, pp.12–17 (in Russian)
- ^ US 4663230, Tennent, Howard G., "Carbon fibrils, method for producing same and compositions containing same", issued 1987-05-05
- ^ Iijima, Sumio (7 November 1991). "Helical microtubules of graphitic carbon". Nature 354 (6348): 56–58. Bibcode 1991Natur.354...56I. doi:10.1038/354056a0.
- ^ Mintmire, J.W.; Dunlap, BI; White, CT (1992). "Are Fullerene Tubules Metallic?". Physical Review Letters 68 (5): 631–634. Bibcode 1992PhRvL..68..631M. doi:10.1103/PhysRevLett.68.631. PMID 10045950.
- ^ Bethune, D. S. et al. (1993). "Cobalt-catalyzed growth of carbon nanotubes with single-atomic-layer walls". Nature 363 (6430): 605–607. Bibcode 1993Natur.363..605B. doi:10.1038/363605a0.
- ^ Iijima, Sumio; Ichihashi, Toshinari (1993). "Single-shell carbon nanotubes of 1-nm diameter". Nature 363 (6430): 603–605. Bibcode 1993Natur.363..603I. doi:10.1038/363603a0.
- ^ "The Discovery of Single-Wall Carbon Nanotubes at IBM". IBM. http://www.almaden.ibm.com/st/past_projects/nanotubes/.
- ^ a b Krätschmer, W.; Lamb, Lowell D.; Fostiropoulos, K.; Huffman, Donald R. (1990). "Solid C60: a new form of carbon". Nature 347 (6291): 354–358. Bibcode 1990Natur.347..354K. doi:10.1038/347354a0.
- ^ Kroto, H. W.; Heath, J. R.; O'Brien, S. C.; Curl, R. F.; Smalley, R. E. (1985). "C60: Buckminsterfullerene". Nature 318 (6042): 162–163. Bibcode 1985Natur.318..162K. doi:10.1038/318162a0.
- NT06 – the major CNT event – click the speakers
- NT05 – click the "HERE"s
- Selection of free-download articles on carbon nanotubes
- Nanohedron.com image gallery with carbon nanotubes
- The stuff of dreams, CNET
- The Nanotube site. Last updated 2009.05.03
- EU Marie Curie Network CARBIO: Multifunctional carbon nanotubes for biomedical applications
- Carbon nanotube on arxiv.org
- C60 and Carbon Nanotubes a short video explaining how nanotubes can be made from modified graphite sheets and the three different types of nanotubes that are formed
- Carbon Nanotubes & Buckyballs.
- The Wondrous World of Carbon Nanotubes
- Learning module for Bandstructure of Carbon Nanotubes and Nanoribbons
- Durability of carbon nanotubes and their potential to cause inflammation by Dr Megan Osmond and others. (SafeWork Australia, May 2011). This was a collaboration between the Institute of Occupational Medicine, Edinburgh University and CSIRO in Australia.
- Durability and inflammogenic impact of carbon nanotubes compared with asbestos fibres. Particle and Fibre Toxicology. 13th March, 2011 (epub ahead of print) by MJ Osmond-McLeod and others.
Allotropes of carbon sp3 forms sp2 forms sp formsLinear acetylenic carbon mixed sp3/sp2 forms other forms related
Wikimedia Foundation. 2010.
Look at other dictionaries:
Carbon Nanotube — Schematische animierte Darstellung der Struktur einer Kohlenstoffnanoröhre Kohlenstoffnanoröhren, auch CNT (englisch carbon nanotubes), sind mikroskopisch kleine röhrenförmige Gebilde (molekulare Nanoröhren) aus Kohlenstoff. Ihre Wände bestehen… … Deutsch Wikipedia
carbon nanotube — noun a fullerene molecule having a cylindrical or toroidal shape • Syn: ↑nanotube • Hypernyms: ↑fullerene … Useful english dictionary
carbon nanotube — noun Any nanostructure, a member of the fullerene family, having graphene layers wrapped into perfect cylinders. Syn: buckytube … Wiktionary
Carbon Nanotube Field Effect Transistor — Le transistor à effet de champ à nanotube (CNFET), utilise un nanotube de carbone mono paroi dans une structure s’apparentant à un transistor à effet de champ (FET)conventionnel Un CNFET (Carbon Nanotube Field Effect Transistor) est un dispositif … Wikipédia en Français
multi-wall carbon nanotube — Multi Wall Carbon Nanotube (MWCNT) Многослойная углеродная нанотрубка … Толковый англо-русский словарь по нанотехнологии. - М.
Carbon fiber — or carbon fibre [See American and British English spelling differences.] (alternately called graphite fiber, graphite fibre or carbon graphite) is a material consisting of extremely thin fibers about 0.0002–0.0004 inches (0.005–0.010 mm) in… … Wikipedia
Carbon nanofiber — Carbon nanofibers are cylindric nanostructures with graphene layers arranged as stacked cones, cups or plates. Carbon nanofibers with graphene layers wrapped into perfect cylinders are called carbon nanotubes.ynthesisCarbon nanofibers are… … Wikipedia
Nanotube nanomotor — A device generating linear or rotational motion using carbon nanotube(s) as the primary component, is termed a nanotube nanomotor. Nature already has some of the most efficient and powerful kinds of nanomotors. Some of these natural biological… … Wikipedia
Carbon nanotubes in photovoltaics — Organic photovoltaic devices (OPVs) are fabricated from thin films of organic semiconductors, such as polymers and small molecule compounds, and are typically on the order of 100 nm thick. Because polymer based OPVs can be made using a coating… … Wikipedia
Nanotube membrane — Not to be confused with membrane nanotube. Part of a series of articles on N … Wikipedia