Forge welding

Forge welding

Forge welding is a welding process of heating two or more pieces of metal and then hammering them together. The process is one of the simplest methods of joining metals and has been used since ancient times. Forge welding is versatile, being able to join a host of similar and dissimilar metals. With the invention of electrical and gas welding methods during the Industrial Revolution, forge welding has been largely replaced.

Forge welding between similar materials is caused by solid-state diffusion. This results in a weld that consists of only the welded materials without any fillers or bridging materials.

Forge welding between dissimilar materials is caused by the formation of a lower melting temperature eutectic between the materials. Due to this the weld is often stronger than the individual metals.

The temperature required to forge weld is typically 50 to 90 percent of the melting temperature, steel welds at a lower temperature than iron. The metal may take on a glossy or wet appearance at the welding temperature, care must be taken to avoid overheating the metal to the point that it gives off sparks from rapid oxidation (burning).

Applications

One of the most famous applications of forge welding is in the production of pattern-welded blades. During the process a billet of steel is repeatedly drawn out, folded back and welded upon itself. Another lesser known application was the manufacture of shotgun barrels. Metal wire was spooled onto a mandrel, and then forged into a barrel that was thin, uniform, and strong. Often such objects are acid etched to expose the underlying pattern of metal which is unique to each item and adds to their aesthetic appeal.

Flux

Often a flux is used to keep the welding surfaces from oxidizing and producing a poor quality weld. The flux also mixes with the oxides that do form and lowers the melting temperature and the viscosity of the oxides. This enables the oxides to flow out of the joint when the two pieces are beaten together. A simple flux can be made from borax, sometimes with the addition of iron filings.

Early examples of flux used different combinations and various amounts of iron fillings, borax, sal ammoniac, balsam of copaiba, cyanide of potash, and soda phosphate. The 1920 edition of Scientific American book of facts and formulae indicates a frequently offered trade secret as using copperas, saltpeter, common salt, black oxide of manganese, prussiate of potash, and "nice welding sand".

ee also

*Pattern welding

External links

* [http://www.msm.cam.ac.uk/phase-trans/2005/Amir/bond.html Forge Welding]


Wikimedia Foundation. 2010.

Игры ⚽ Поможем решить контрольную работу

Look at other dictionaries:

  • Forge welding — Forge welding. См. Кузнечная сварка. (Источник: «Металлы и сплавы. Справочник.» Под редакцией Ю.П. Солнцева; НПО Профессионал , НПО Мир и семья ; Санкт Петербург, 2003 г.) …   Словарь металлургических терминов

  • forge welding — the welding of pieces of hot metal with pressure or blows. * * * …   Universalium

  • forge welding — noun : the uniting of two pieces of hot metal by hammering them together on an anvil * * * the welding of pieces of hot metal with pressure or blows …   Useful english dictionary

  • forge welding — Смотри печная сварка труб …   Энциклопедический словарь по металлургии

  • forge welding mill — Смотри агрегат печной сварки …   Энциклопедический словарь по металлургии

  • Welding — is a fabrication process that joins materials, usually metals or thermoplastics, by causing coalescence. This is often done by melting the workpieces and adding a filler material to form a pool of molten material (the weld puddle ) that cools to… …   Wikipedia

  • welding — Technique for joining metallic parts, usually through the application of heat. Discovered in the 1st millennium AD during attempts to manipulate iron into useful shapes, the technique produced a strong, tough blade. Welding traditionally involved …   Universalium

  • Forge — For the process of shaping metal by localized compressive forces, see Forging. For other uses, see Forge (disambiguation). A blacksmith s coal forge …   Wikipedia

  • forge iron — suvirinimo geležis statusas T sritis chemija apibrėžtis Techniškai gryna geležis, kurioje yra ypač mažai C ir Mn (≤ 0,02%). atitikmenys: angl. forge iron; welding iron; wrought iron rus. сварочное железо …   Chemijos terminų aiškinamasis žodynas

  • welding iron — suvirinimo geležis statusas T sritis chemija apibrėžtis Techniškai gryna geležis, kurioje yra ypač mažai C ir Mn (≤ 0,02%). atitikmenys: angl. forge iron; welding iron; wrought iron rus. сварочное железо …   Chemijos terminų aiškinamasis žodynas

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”