- 6061 aluminium alloy
6061 is an
aluminium alloy , withmagnesium andsilicon as the alloying elements. It has generally good mechanical properties and is heat treatable and weldable. It is one of the most common alloys of aluminum for general purpose use.It is commonly produced in several heat temper grades, 6061-O, 6061-T4, 6061-T6, 6061-T651, 6061-T42.
Basic properties
6061 has a
density of 2.70 g/cm³ (0.0975 lb/in³).Chemical composition
The alloy composition of 6061 is:
*Silicon minimum 0.4%, maximum 0.8% by weight
*Iron no minimum, maximum 0.7%
*Copper minimum 0.15%, maximum 0.40%
*Manganese no minimum, maximum 0.15%
*Magnesium minimum 0.8%, maximum 1.2%
*Chromium minimum 0.04%, maximum 0.35%
*Zinc no minimum, maximum 0.25%
*Titanium no minimum, maximum 0.15%
* Other elements no more than 0.05% each, 0.15% total
* RemainderAluminum Mechanical properties
The mechanical properties of 6061 depend greatly on the temper, or heat treatment, of the material. [http://www.alcoa.com/adip/catalog/pdf/Extruded_Alloy_6061.pdf Alcoa 6061 data sheet] (pdf), accessed October 13, 2006]
6061-0
Annealed 6061 (6061-0 temper) has maximum
tensile strength no more than 18,000 psi (125 MPa), and maximumyield strength no more than 8,000 psi (55 MPa). The material has elongation (stretch before ultimate failure) of 25-30 %.6061-T4
T4 temper 6061 has an ultimate tensile strength of at least 30,000 psi (207 MPa) and yield strength of at least 16,000 psi (110 MPa). It has elongation of 16%.
6061-T6
T6 temper 6061 has an ultimate tensile strength of at least 42,000 psi (290 MPa) and yield strength of at least 35,000 psi (241 MPa). In thicknesses of 0.250 inch (6.35 mm) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%. T651 temper has similar mechanical properties. The famous
Pioneer plaque was made of this particular alloy.Uses
6061 is widely used for construction of
aircraft structures, such aswing s andfuselage s, more commonly inhomebuilt aircraft than commercial or military aircraft. [http://www.aircraftspruce.com/catalog/mepages/aluminfo.php Aluminum Information at aircraftspruce.com] , accessed October 13, 2006]6061 is used for
yacht construction, including small utilityboat s."Boatbuilding with Aluminum", Stephen F. Pollard, 1993, ISBN 0-07-050426-1]6061 is commonly used in the construction of Bicycle Frames and components. The Cycling industry also uses 7005 and 7075 aluminium alloys.
Welding
6061 is highly weldable, for example using
tungsten inert gas welding (TIG) ormetal inert gas welding (MIG). Typically, after welding, the properties near the weld are those of 6061-0, a loss of strength of around 80%. The material can be re-heat-treated to restore -T4 or -T6 temper for the whole piece.Extrusions
6061 is also an alloy used in the production of
extrusion s—long constant–cross-section structural shapes produced by pushing metal through a shaped die.Forgings
6061 is also an alloy that is commonly used in a hot forging. The billet is heated thru an induction furnance and forged using a closed die process. Automotive parts, Recreational ATV parts, Industrial parts are just some if the uses as an forging.