Evaporation (deposition)

Evaporation (deposition)
Evaporation machine used for metallization at LAAS technological facility in Toulouse, France.

Evaporation is a common method of thin film deposition. The source material is evaporated in a vacuum. The vacuum allows vapor particles to travel directly to the target object (substrate), where they condense back to a solid state. Evaporation is used in microfabrication, and to make macro-scale products such as metallized plastic film.


Physical principle

Evaporation involves two basic processes: a hot source material evaporates and condenses on the substrate. It resembles the familiar process by which liquid water appears on the lid of a boiling pot. However, the gaseous environment and heat source (see "Equipment" below) are different.

Evaporation takes place in a vacuum, i.e. vapors other than the source material are almost entirely removed before the process begins. In high vacuum (with a long mean free path), evaporated particles can travel directly to the deposition target without colliding with the background gas. (By contrast, in the boiling pot example, the water vapor pushes the air out of the pot before it can reach the lid.) At a typical pressure of 10-4 Pa, an 0.4-nm particle has a mean free path of 60 m. Hot objects in the evaporation chamber, such as heating filaments, produce unwanted vapors that limit the quality of the vacuum.

Evaporated atoms that collide with foreign particles may react with them; for instance, if aluminium is deposited in the presence of oxygen, it will form aluminium oxide. They also reduce the amount of vapor that reaches the substrate, which makes the thickness difficult to control.

Evaporated materials deposit nonuniformly if the substrate has a rough surface (as integrated circuits often do). Because the evaporated material attacks the substrate mostly from a single direction, protruding features block the evaporated material from some areas. This phenomenon is called "shadowing" or "step coverage."

When evaporation is performed in poor vacuum or close to atmospheric pressure, the resulting deposition is generally non-uniform and tends not to be a continuous or smooth film. Rather, the deposition will appear fuzzy .


Any evaporation system includes a vacuum pump. It also includes an energy source that evaporates the material to be deposited. Many different energy sources exist:

  • In the thermal method, metal wire is fed onto heated semimetal (ceramic) evaporators known as "boats" due to their shape. A pool of melted metal forms in the boat cavity and evaporates into a cloud above the source. Alternatively the source material is placed in a crucible, which is radiatively heated by an electric filament, or the source material may be hung from the filament itself (filament evaporation).
  • In the electron-beam method, the source is heated by an electron beam with an energy up to 15 keV.
  • In flash evaporation, a fine wire of source material is fed continuously onto a hot ceramic bar, and evaporates on contact.
  • Resistive evaporation is accomplished by passing a large current through a resistive wire or foil containing the material to be deposited. The heating element is often referred to as an "evaporation source". Wire type evaporation sources are made from tungsten wire and can be formed into filaments, baskets, heaters or looped shaped point sources. Boat type evaporation sources are made from tungsten, tantalum, molybdenum or ceramic type materials capable of withstanding high temperatures.

Some systems mount the substrate on an out-of-plane planetary mechanism. The mechanism rotates the substrate simultaneously around two axes, to reduce shadowing.


  • Purity of the deposited film depends on the quality of the vacuum, and on the purity of the source material.
  • The thickness of the film will vary due to the geometry of the evaporation chamber. Collisions with residual gases aggravate nonuniformity of thickness.
  • Filament and resistive evaporation cannot deposit thick films, because the size of the filament limits the amount of material that can be deposited. However, flash evaporation and methods that use crucibles can deposit thick films.
  • In order to deposit a material, the evaporation system must be able to melt it. This makes refractory materials such as tungsten hard to deposit by methods that do not use electron-beam heating.
  • Electron-beam evaporation allows tight control of the evaporation rate. Thus, an electron-beam system with multiple beams and multiple sources can deposit a chemical compound or composite material of known composition.
  • Step coverage


An important example of an evaporative process is the production of aluminized PET film packaging film in a roll-to-roll web system. Often, the aluminum layer in this material is not thick enough to be entirely opaque since a thinner layer can be deposited more cheaply than a thick one. The main purpose of the aluminum is to isolate the product from the external environment by creating a barrier to the passage of light, oxygen, or water vapor.

Evaporation is commonly used in microfabrication to deposit metal films.

Comparison to other deposition methods

  • Alternatives to evaporation, such as sputtering and chemical vapor deposition, have better step coverage. This may be an advantage or disadvantage, depending on the desired result.
  • Sputtering tends to deposit material more slowly than evaporation.
  • Sputtering uses a plasma, which produces many high-speed atoms that bombard the substrate and may damage it. Evaporated atoms have a Maxwellian energy distribution, determined by the temperature of the source, which reduces the number of high-speed atoms. However, electron beams tend to produce X-rays (Bremsstrahlung) and stray electrons, each of which can also damage the substrate.


  • Jaeger, Richard C. (2002). "Film Deposition". Introduction to Microelectronic Fabrication. Upper Saddle River: Prentice Hall. ISBN 0-201-44494-7. 
  • Semiconductor Devices: Physics and Technology, by S.M. Sze, ISBN 0-471-33372-7, has an especially detailed discussion of film deposition by evaporation.
  • R. D. Mathis Company Evaporation Sources Catalog, by R. D. Mathis Company, pages 1 through 7 and page 12, 1992.

External links

Wikimedia Foundation. 2010.

Look at other dictionaries:

  • evaporation deposition — garinis nusodinimas statusas T sritis radioelektronika atitikmenys: angl. evaporation deposition; vapor deposition; vapor phase deposition vok. Abscheidung aus der Dampfphase, f; Dampfphasenabscheidung, f rus. осаждение из паровой фазы, n pranc.… …   Radioelektronikos terminų žodynas

  • déposition en phase vapeur — garinis nusodinimas statusas T sritis radioelektronika atitikmenys: angl. evaporation deposition; vapor deposition; vapor phase deposition vok. Abscheidung aus der Dampfphase, f; Dampfphasenabscheidung, f rus. осаждение из паровой фазы, n pranc.… …   Radioelektronikos terminų žodynas

  • Evaporation — is the process by which molecules in a liquid state (e.g. water) spontaneously become gaseous (e.g. water vapor). It is the opposite of condensation. Generally, evaporation can be seen by the gradual disappearance of a liquid when exposed to a… …   Wikipedia

  • Évaporation sous vide — Système de métallisation par évaporation sous vide du laboratoire LAAS de Toulouse. L évaporation sous vide est une technique de dépôt de couche mince (généralement métallique), utilisé notamment dans la fabrication micro électronique. Le… …   Wikipédia en Français

  • Deposition (phase transition) — This diagram shows the nomenclature for the different phase transitions. Deposition is a process in which gas transforms into solid (also known as desublimation). The reverse of deposition is sublimation. One example of deposition is the process… …   Wikipedia

  • evaporation — užgarinimas statusas T sritis fizika atitikmenys: angl. evaporation; vapor deposition; vapour deposition vok. Aufdampfung, f; Bedampfung, f rus. нанесение испарением, n pranc. dépôt en phase vapeur, m …   Fizikos terminų žodynas

  • Évaporation par faisceau d'électrons — L’évaporation par faisceau d électrons est une technique qui consiste à évaporer un matériau placé dans un creuset porté à haute température, soit par un courant traversant une nacelle résistive (effet Joule), soit par le bombardement d un… …   Wikipédia en Français

  • Déposition sous vide — Dépôt sous vide Sommaire 1 But 2 Principe 3 Contraintes particulières 4 Avantages et inconvénients …   Wikipédia en Français

  • Vacuum deposition — Not to be confused with Vacuum coating. Vacuum deposition is a family of processes used to deposit layers atom by atom or molecule by molecule at sub atmospheric pressure (vacuum) on a solid surface. The layers may be as thin as one atom to… …   Wikipedia

  • vapor deposition — garinis nusodinimas statusas T sritis radioelektronika atitikmenys: angl. evaporation deposition; vapor deposition; vapor phase deposition vok. Abscheidung aus der Dampfphase, f; Dampfphasenabscheidung, f rus. осаждение из паровой фазы, n pranc.… …   Radioelektronikos terminų žodynas

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”

We are using cookies for the best presentation of our site. Continuing to use this site, you agree with this.