White Portland cement

White Portland cement

White Portland cement or white ordinary Portland cement (WOPC) is similar to ordinary, gray Portland cement in all respects except for its high degree of whiteness. Obtaining this color requires substantial modification to the method of manufacture, and because of this, it is somewhat more expensive than the gray product.

Contents

Uses

White Portland cement is used in combination with white aggregates to produce white concrete for prestige construction projects and decorative work. White concrete usually takes the form of pre-cast cladding panels, since it is not economical to use white cement for structural purposes. White Portland cement is also used in combination with inorganic pigments to produce brightly colored concretes and mortars. Ordinary cement, when used with pigments, produces colors that may be attractive, but are somewhat dull. With white cement, bright reds, yellows and greens can be readily produced. Blue concrete can also be made, at some expense. The pigments may be added at the concrete mixer. Alternatively, to guarantee repeatable color, some manufacturers supply ready-blended colored cements, using white cement as a base. The whiteness of WOPC is measured as the powdered material having a reflectance value ("L value") in excess of 85%. A particular success in the use of WOPC and added pigments is monocouche renders.

Manufacture

Rawmix formulation

The characteristic greenish-gray to brown color of ordinary Portland cement derives from a number of transitional elements in its chemical composition. These are, in descending order of coloring effect, chromium, manganese, iron, copper, vanadium, nickel and titanium. The amount of these in white cement is minimized as far as possible. Cr2O3 is kept below 0.003%, Mn2O3 is kept below 0.03%, and Fe2O3 is kept below 0.35% in the clinker. The other elements are usually not a significant problem. Portland cement is usually made from cheap, quarried raw materials, and these usually contain substantial amounts of Cr, Mn and Fe. For example, limestones used in cement manufacture usually contain 0.3-1% Fe2O3, whereas levels below 0.1% are sought in limestones for white manufacture. Typical clays used in gray cement rawmix may contain 5-15% Fe2O3. Levels below 0.5% are desirable, and conventional clays are usually replaced with kaolin. Kaolin is fairly low in SiO2, and so a large amount of sand is usually also included in the mix. Iron and manganese usually occur together in nature, so that selection of low-iron materials usually ensures that manganese content is also low, but chromium can arise from other sources, notably from the wear of chrome steel grinding equipment during the production of rawmix. See rawmill. This wear is exacerbated by the high sand-content of the mix, which makes it extremely abrasive. Furthermore, to make a combinable rawmix, the sand must be ground to below 45 μm particle diameter. Often this is achieved by grinding the sand separately, using ceramic grinding media to reduce contamination.

Kiln operation

In general, the rotary kilns used to chemically combine the raw materials are operated at a higher peak temperature (1450-1500°C) than that required for gray clinker manufacture (1400-1450°C). This requires a higher fuel consumption (typically 20-50% more), and results in lower kiln output (typically 20-50% less) for a given sized kiln. The reason for this is the relatively small amount of liquid produced during sintering, because of the low iron-content of the mix. The final reaction in the kiln, conversion of belite to alite, requires the melt liquid as a solvent, and is slower if the amount of melt is low. This can be partially compensated by adding to the rawmix a combination of calcium sulfate and fluoride in the form of calcium fluoride or waste cryolite. This combination reduces the reaction temperature. In cases where the clinker Fe2O3 content is above 0.2% (which is almost always the case), the unique processes of "bleaching" and "quenching" are also employed. "Bleaching" involves directing a second flame (apart from that used to heat the kiln) onto the bed of clinker close to the kiln exit to reduce Fe(III) to Fe(II). This reduction is rigorously avoided in gray cement production, because of the deleterious effect it can have on clinker quality. But in white clinker production, where the iron content is low, this is not an issue. Subsequently, to prevent the re-oxidation of the iron, "quenching" is performed. This consists of rapidly lowering the clinker temperature from 1200°C to below 600°C in a few seconds, as it leaves the kiln. This usually involves dropping it into cold water. This contributes to the relatively poor energy efficiency of the process, since the sensible heat of the clinker is not recycled as in normal clinker manufacturer

Clinker grinding and handling

The clinker is next ground to cement (perhaps after a drying stage). Here calcium sulfate is added to control set, in the form of a high-purity grade of gypsum or anhydrite. In some specifications (not ASTM), a small amount of titanium dioxide may be added to improve reflectance. At all stages, great care is needed to avoid contamination with colored materials.

Specifications

White Portland cement differs physically from gray cement only in terms of its color. Its setting behavior and strength development are essentially the same as that expected in gray cement, and it meets standard specifications such as ASTM C 150 and EN 197. In practice, because much white cement is used in pre-cast concrete products, it is commonly made to a high-early strength specification such as ASTM C 150 Type III. This aids concrete manufacturers' production rate. Higher potential strength also helps to counteract the strength-diminishing effects of pigment addition. In addition to the usual specifications, manufacturers guarantee the whiteness of the product, typically in terms of a reflectance measurement, such as L*a*b L-value, or tristimulus. In the latter case, because off-color white cement tends to be greenish, the Tri-Y (green) value is used. Because the color so much depends upon the "bleaching" and "quenching" operations, merely specifying a low iron content does not guarantee good whiteness.

See also


Wikimedia Foundation. 2010.

Игры ⚽ Поможем решить контрольную работу

Look at other dictionaries:

  • Portland cement — is the most common type of cement in general usage in many parts of the world, as it is a basic ingredient of concrete, mortar, stucco and most non specialty grout. It is a fine powder produced by Portland cement clinker (more than 90%), a… …   Wikipedia

  • cement — cementable, adj. cementer, n. cementless, adj. /si ment /, n. 1. any of various calcined mixtures of clay and limestone, usually mixed with water and sand, gravel, etc., to form concrete, that are used as a building material. 2. any of various… …   Universalium

  • Cement — In the most general sense of the word, a cement is a binder, a substance which sets and hardens independently, and can bind other materials together. The name cement goes back to the Romans who used the term opus caementicium to describe masonry… …   Wikipedia

  • Portland stone — is a limestone from the Jurassic period quarried on the Isle of Portland, Dorset. The quarries consist of beds of white grey limestone separated by chert beds. It has been used extensively throughout the British Isles, notably in major public… …   Wikipedia

  • white cement — noun : a portland cement made from raw materials very low in the iron compounds that give the gray color to the usual portland cement …   Useful english dictionary

  • cement — I (New American Roget s College Thesaurus) n. mortar, concrete, grout, Portland cement; adhesive, glue, mucilage, paste. See connection, coherence, unity. II (Roget s IV) n. Syn. glue, lute, lime, putty, tar, gum, mortar, paste, solder, adhesive …   English dictionary for students

  • Isle of Portland — infobox UK place country = England official name= Isle of Portland map type = Dorset latitude= 50.550 longitude= 2.440 population = 12,710cite web| year = 2005 | url = http://www.dorsetforyou.com/index.jsp?articleid=343603 | title=Portland… …   Wikipedia

  • James Frost (cement maker) — James Frost (1780? 1840?) was a British cement manufacturer, and invented processes that led to the eventual development of Portland cement.James Frost was born in Finchley, North London, England [Francis A J, The Cement Industry 1796 1914 ,… …   Wikipedia

  • Charles Richardson (cement merchant) — Charles Richardson (born February 16, 1817 Born in Woodford, London, Essex, United Kingdom) Founder of the family Brick and Cement Firm A WT Richardson Ltd, which lasted over 100 years. This business was founded by the late Charles Richardson in… …   Wikipedia

  • James Parker (cement maker) — James Parker was a British clergyman and cement manufacturer who invented one of the pioneering new cements of the late eighteenth century.In 1791, he was granted a patent Method of Burning bricks, Tiles, Chalk . His second patent in 1796 A… …   Wikipedia

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”