Neodymium(III) chloride

Neodymium(III) chloride
Other names Neodymium trichloride
Identifiers
CAS number	10024-93-8 Y,  13477-89-9 (hydrate)
ChemSpider	59589 Y
Jmol-3D images	Image 1
SMILES Cl[Nd](Cl)Cl
InChI InChI=1S/3ClH.Nd/h3*1H;/q;;;+3/p-3 Y Key: ATINCSYRHURBSP-UHFFFAOYSA-K Y InChI=1/3ClH.Nd/h3*1H;/q;;;+3/p-3 Key: ATINCSYRHURBSP-DFZHHIFOAM
Properties
Molecular formula	NdCl3, NdCl3·6H2O (hydrate)
Molar mass	250.598 g/mol
Appearance	mauve-colored powder hygroscopic
Density	4.13 g/cm3 (2.282 for hydrate)
Melting point	758 °C
Boiling point	1600 °C
Solubility in water	0.967 kg/L at 13 °C
Solubility in ethanol	0.445 kg/L
Structure
Crystal structure	hexagonal (UCl3 type), hP8
Space group	P63/m, No. 176
Coordination geometry	Tricapped trigonal prismatic (nine-coordinate)
Hazards
MSDS	External MSDS
EU Index	Not listed
Related compounds
Other anions	Neodymium(III) bromide
Other cations	LaCl3, SmCl3, PrCl3, EuCl3, CeCl3, GdCl3, TbCl3
Y chloride (verify) (what is: Y/N?) Except where noted otherwise, data are given for materials in their standard state (at 25 °C, 100 kPa)
Infobox references

Neodymium(III) chloride or neodymium trichloride is a chemical compound of neodymium and chlorine with the formula NdCl₃. This anhydrous compound is a mauve-colored solid that rapidly absorbs water on exposure to air to form a purple-colored hexahydrate, NdCl₃·6H₂O. Neodymium(III) chloride is produced from minerals monazite and bastnäsite using a complex multistage extraction process. The chloride has several important applications as an intermediate chemical for production of neodymium metal and neodymium-based lasers and optical fibers. Other applications include a catalyst in organic synthesis and in decomposition of waste water contamination, corrosion protection of aluminium and its alloys, and fluorescent labeling of organic molecules (DNA).

Appearance

NdCl₃ under sunlight (top) and fluorescent light (bottom)

NdCl₃ is a mauve colored hygroscopic solid whose color changes to purple upon absorption of atmospheric water. The resulting hydrate, like many other neodymium salts, has the interesting property that it instantly and reversibly turns light yellow under fluorescent light (see picture).^[1] The color change is likely due to the charge transfer converting the Nd³⁺ ions into the Nd²⁺ state; the orange absorption band of Nd³⁺ decreases and the green Nd²⁺ absorption increases producing the yellowish color.^[2][3]

Structure

Solid

The anhydrous NdCl₃ features Nd in a nine-coordinate tricapped trigonal prismatic geometry and crystallizes with the UCl₃ structure. This hexagonal structure is common for many halogenated lanthanides and actinides such as LaCl₃, LaBr₃, SmCl₃, PrCl₃, EuCl₃, CeCl₃, CeBr₃, GdCl₃, AmCl₃ and TbCl₃ but not for YbCl₃ and LuCl₃.^[4]

Solution

The structure of neodymium(III) chloride in solution crucially depends on the solvent: In water, the major species are Nd(H₂O)₈³⁺, and this situation is common for most rare earth chlorides and bromides. In methanol, the species are NdCl₂(CH₃OH)₆⁺ and in hydrochloric acid NdCl(H₂O)₇²⁺. The coordination of neodymium is octahedral (8-fold) in all cases, but the ligand structure is different.^[5]

Properties

NdCl₃ is a soft paramagnetic solid, which turns ferromagnetic at very low temperature of 0.5 K.^[6] Its electrical conductivity is about 240 S/m and heat capacity is ~100 J/(mol·K).^[7] NdCl₃ is readily soluble in water and ethanol, but not in chloroform or ether. Reduction of NdCl₃ with Nd metal at temperatures above 650 °C yields NdCl₂:^[8]

2 NdCl₃ + Nd → 3 NdCl₂

Heating of NdCl₃ with water vapors or silica produces neodymium oxochloride:

NdCl₃ + H₂O → NdOCl + 2 HCl

2 NdCl₃ + SiO₂O → 2 NdOCl + SiCl₄

Reacting NdCl₃ with hydrogen sulfide at about 1100 °C produces neodymium sulfide:

2 NdCl₃ + 3 H₂S → 2 Nd₂S₃ + 6 HCl

Reactions with ammonia and phosphine at high temperatures yield neodymium nitride and phosphide, respectively:

NdCl₃ + NH₃ → NdN + 3 HCl

NdCl₃ + PH₃ → NdP + 3 HCl

Whereas the addition of hydrofluoric acid produces neodymium fluoride:^[9]

NdCl₃ + 3 HF → NdF₃ + 3 HCl

Preparation

Monazite

NdCl₃ is produced from minerals monazite and bastnäsite. The synthesis is complex because of the low abundance of neodymium in the Earth's crust (38 mg/kg) and because of difficulty of separating neodymium from other lanthanides. The process is however easier for neodymium than for other lanthanides because of its relatively high content in the mineral - up to 16% by weight, which is the third highest after cerium and lanthanum.^[10] Many synthesis varieties exist and one can be simplified as follows:

The crushed mineral is treated with hot concentrated sulfuric acid to produce water-soluble sulfates of rare earths. The acidic filtrates are partially neutralized with sodium hydroxide to pH 3-4. Thorium precipitates out of solution as hydroxide and is removed. After that the solution is treated with ammonium oxalate to convert rare earths in to their insoluble oxalates. The oxalates are converted to oxides by annealing. The oxides are dissolved in nitric acid that excludes the main components, cerium, whose oxide is insoluble in HNO₃. Neodymium oxide is separated from other rare-earth oxides by ion exchange. In this process, rare-earth ions are adsorbed onto suitable resin by ion exchange with hydrogen, ammonium or cupric ions present in the resin. The rare earth ions are then selectively washed out by suitable complexing agent, such as ammonium citrate or nitrilotracetate.^[9]

This process normally yields Nd₂O₃; the oxide is difficult to directly convert to elemental neodymium, which is often the goal of the whole technological procedure. Therefore the oxide is treated with hydrochloric acid or ammonium chloride to produce the less stable NdCl₃:^[9]

Nd₂O₃ + 6 NH₄Cl → 2 NdCl₃ + 3 H₂O + 6 NH₃

The thus produced NdCl₃ quickly absorbs water and converts to NdCl₃·6H₂O hydrate, which is stable for storage, and can be converted back into NdCl₃ when necessary. Simple rapid heating of the hydrate is not practical for that purpose because it causes hydrolysis with consequent production of Nd₂O₃.^[11] Therefore anhydrous NdCl₃ is prepared by dehydration of the hydrate either by slowly heating to 400 °C with 4-6 equivalents of ammonium chloride under high vacuum, or by heating with an excess of thionyl chloride for several hours.^{[4][12][13][14]} The NdCl₃ can alternatively be prepared by reacting neodymium metal with hydrogen chloride or chlorine, though this method is not economical due to the relatively high price of the metal and is used for research purposes only. After preparation, it is usually purified by high temperature sublimation under high vacuum.^[4][15][16]

Applications

Production of neodymium metal

Nd:YAG laser with lid open showing frequency doubled 532 nm green light

Neodymium(III) chloride is the most common starting compound for production of neodymium metal. NdCl₃ is heated with ammonium chloride or ammonium fluoride and hydrofluoric acid or with alkali or alkaline earth metals in vacuum or argon atmosphere at 300-400 °C.

LaCl₃ + 3 Li → La + 3 LiCl

An alternative route is electrolysis of molten mixture of anhydrous LaCl₃ and NaCl or KCl at temperatures about 700 °C. The mixture does melt at those temperatures, even though they are lower than the melting points of NdCl₃ and KCl (~770 °C).^[17]

Lasers and fiber amplifiers

Although NdCl₃ itself does not have strong luminescence,^[18] it serves as a source of Nd³⁺ ions for various light emitting materials. The latter include Nd-YAG lasers and Nd-doped optical fiber amplifiers, which amplify light emitted by other lasers. The Nd-YAG laser emits infrared light at 1.064 micrometres and is the most popular solid-state laser (i.e. laser based on a solid medium). The reason for using NdCl₃ rather than metallic neodymium or its oxide, in fabrication of fibers is easy decomposition of NdCl₃ during the chemical vapor deposition; the latter process is widely used for the fiber grows.^[19]

Neodymium(III) chloride is a dopant not only of traditional silica-based optical fibers, but of plastic fibers (dopedphotolime-gelatin, polyimide, polyethylene, etc.) as well.^[20] It is also used in as an additive into infrared organic light-emitting diodes.^[21][22] Besides, neodymium doped organic films can not only act as LEDs, but also as color filters improving the LED emission spectrum.^[23]

Solubility of neodymium(III) chloride (and other rare-earth salts) is various solvents results in a new type of rare-earth laser, which uses not a solid but liquid as an active medium. The liquid containing Nd³⁺ ions is prepared in the following reactions:

SnCl₄ + 2 SeOCl₂ → SnCl₆²⁻ + 2 SeOCl⁺

SbCl₅ + SeOCl₂ → SbCl₆²⁻ + SeOCl⁺

3 SeOCl⁺ + NdCl₃ → Nd³⁺(solv) + 3 SeOCl₂,

where Nd³⁺ is in fact the solvated ion with several selenium oxychloride molecules coordinated in the first coordination sphere, that is [Nd(SeOCl₂)_m]³⁺. The laser liquids prepared by this technique emits at the same wavelength of 1.064 micrometres and possess properties, such as high gain and sharpness of the emission, that are more characteristic of crystalline than Nd-glass lasers. The quantum efficiency of those liquid lasers was about 0.75 relative to the traditional Nd:YAG laser.^[21]

Catalysis

Another important application of NdCl₃ is in catalysis—in combination with organic chemicals, such as triethylaluminium and 2-propanol, it accelerates polymerization of various dienes. The products include such general purpose synthetic rubbers as polybutylene, polybutadiene, and polyisoprene.^[11][24][25]

Neodymium(III) chloride is also used to modify titanium dioxide. The latter is one of the most popular inorganic photocatalyst for decomposition of phenol, various dyes and other waste water contaminants. The catalytic action of titanium oxide has to be activated by UV light, i.e. artificial illumination. However, modifying titanium oxide with neodymium(III) chloride allows catalysis under visible illumination, such as sun light. The modified catalyst is prepared by chemical coprecipitation–peptization method by ammonium hydroxide from mixture of TiCl₄ and NdCl₃ in aqueous solution). This process is used commercially on large scale on 1000 liter reactor for using in photocatalytic self-cleaning paints.^[26][27]

Corrosion protection

Other applications are being developed. For example, it was reported that coating of aluminium or various aluminium alloys produces very corrosion-resistance surface, which then resisted immersion into concentrated aqueous solution of NaCl for two months without sign of pitting. The coating is produced either by immersion into aqueous solution of NdCl₃ for a week or by electrolytic deposition using the same solution. In comparison with traditional chromium based corrosion inhibitors, NdCl₃ and other rare-earth salts are environment friendly and much less toxic to humans and animals.^[28][29]

The protective action of NdCl₃ on aluminium alloys is based on formation of insoluble neodymium hydroxide. Being a chloride, NdCl₃ itself is a corrosive agent, which is sometimes used for corrosion testing of ceramics.^[30]

Labeling of organic molecules

Lanthanides, including neodymium are famous for their bright luminescence and therefore are widely used as fluorescent labels. In particular, NdCl₃ has been incorporated into organic molecules, such as DNA, which could be then easily traced using a fluorescence microscope during various physical and chemical reactions.^[21]

Health issues

Neodymium(III) chloride does not seem toxic to humans and animals (approximately similar to table salt). The LD₅₀ (dose at which there is 50% mortality) for animals is about 3.7 g per kg of body weight (mouse, oral), 0.15 g/kg (rabbit, intravenous injection). Mild irritation of skin occurs upon exposure with 500 mg during 24 hrs (Draize test on rabbits).^[31][32] Substances with LD₅₀ above 2 g/kg are considered non-toxic.^[33]

See also

• Lanthanoid
• Neodymium-doped yttrium lithium fluoride

References

1. ^ Michael O'Donoghue, Robert Webster (2006). Gems. Butterworth-Heinemann. p. 523. ISBN 0750658568. http://books.google.com/?id=ZwcM5H-wHNoC&pg=PA523. 
2. ^ Yamana, Hajimu; Park, Byung Gi; Shirai, Osamu; Fujii, Toshiyuki; Uehara, Akihiro; Moriyama, Hirotake (2006). "Electrochemically produced divalent neodymium in chloride melt". Journal of Alloys and Compounds 408-412: 66. doi:10.1016/j.jallcom.2005.04.104. 
3. ^ Terakado, O; El Abedin, Sherif Zein; Endres, Frank; Nattland, Detlef; Freyland, Werner (2002). "Intervalence charge transfer in neodymium–neodymium chloride melts: spectroscopic and electrical conductivity study". Journal of Non-Crystalline Solids 312-314: 459. doi:10.1016/S0022-3093(02)01714-3. 
4. ^ ^{a b c} F. T. Edelmann, P. Poremba (1997). W. A. Herrmann. ed. Synthetic Methods of Organometallic and Inorganic Chemistry Vol. 6. Stuttgart: Georg Thieme Verlag. 
5. ^ Steele, Marcus L.; Wertz, David L. (1977). "Solvent effects on the coordination of neodymium(3+) ions in concentrated neodymium trichloride solutions". Inorganic Chemistry 16: 1225. doi:10.1021/ic50171a050. 
6. ^ Skjeltorp, A (1977). "Analysis of magnetothermal parameters in NdCl3". Physica B+C 86-88: 1295. doi:10.1016/0378-4363(77)90888-9. 
7. ^ R. T. Carlin (1996). Molten Salts. The Electrochemical Society. p. 447. ISBN 1566771595. http://books.google.com/?id=UWoEjb_BZFQC&pg=PA447. 
8. ^ Gerd Meyer, Lester R. Morss (1991). Synthesis of lanthanide and actinide compounds. Springer. p. 161. ISBN 0792310187. http://books.google.com/?id=bnS5elHL2w8C&pg=PA161. 
9. ^ ^{a b c} Patnaik, Pradyot (2003). Handbook of Inorganic Chemical Compounds. McGraw-Hill. pp. 444–446. ISBN 0070494398. http://books.google.com/?id=Xqj-TTzkvTEC&pg=PA243. Retrieved 2009-06-06. 
10. ^ John Emsley (2003). Nature's building blocks: an A-Z guide to the elements. Oxford University Press. pp. 268–270. ISBN 0198503407. http://books.google.com/?id=j-Xu07p3cKwC. 
11. ^ ^{a b} O. Nuyken, R. Anwander (2006). Neodymium based Ziegler catalysts. Springer. p. 15. ISBN 3540348093. http://books.google.com/?id=xX9mYOp2HFYC&pg=PA15. 
12. ^ M. D. Taylor, P. C. Carter (1962). "Preparation of anhydrous lanthanide halides, especially iodides". J. Inorg. Nucl. Chem. 24: 387. doi:10.1016/0022-1902(62)80034-7. 
13. ^ J. Kutscher, A. Schneider (1971). "Notiz zur Präparation von wasserfreien Lanthaniden-Haloge-niden, Insbesondere von Jodiden". Inorg. Nucl. Chem. Lett. 7: 815. doi:10.1016/0020-1650(71)80253-2. 
14. ^ J. H. Freeman, M. L. Smith (1958). "The preparation of anhydrous inorganic chlorides by dehydration with thionyl chloride". J. Inorg. Nucl. Chem. 7: 224. doi:10.1016/0022-1902(58)80073-1. 
15. ^ L. F. Druding, J. D. Corbett (1961). "Lower Oxidation States of the Lanthanides. Neodymium(II) Chloride and Iodide". J. Am. Chem. Soc. 83: 2462. doi:10.1021/ja01472a010. 
16. ^ J. D. Corbett (1973). Rev. Chim. Minerale 10: 239. 
17. ^ C. K. Gupta, Nagaiyar Krishnamurthy (2004). Extractive metallurgy of rare earths. CRC Press. p. 276. ISBN 0415333407. http://books.google.com/?id=E1npz8pwmYwC&pg=PA276. 
18. ^ B. Henderson, Ralph H. Bartram (2000). Crystal field engineering of solid state laser materials. Cambridge University Press. p. 211. ISBN 0521593492. http://books.google.com/?id=7wM9EQ1oDLwC&pg=PA211. 
19. ^ Emil Wolf (1993). Progress in Optics. Elsevier. p. 49. ISBN 0444815929. http://books.google.com/?id=7mXhWv9f1tIC&pg=PA49. 
20. ^ Wong, W; Liu, K; Chan, K; Pun, E (2006). "Polymer devices for photonic applications". Journal of Crystal Growth 288: 100. doi:10.1016/j.jcrysgro.2005.12.017. 
21. ^ ^{a b c} Comby, S; Bunzli, J (2007). Chapter 235 Lanthanide Near-Infrared Luminescence in Molecular Probes and Devices. 37. pp. 217. doi:10.1016/S0168-1273(07)37035-9. 
22. ^ Oriordan, A; Vandeun, R; Mairiaux, E; Moynihan, S; Fias, P; Nockemann, P; Binnemans, K; Redmond, G (2008). "Synthesis of a neodymium-quinolate complex for near-infrared electroluminescence applications". Thin Solid Films 516: 5098. doi:10.1016/j.tsf.2007.11.112. 
23. ^ Cho, Y.; Choi, Y. K.; Sohn, S. H. (2006). "Optical properties of neodymium-containing polymethylmethacrylate films for the organic light emitting diode color filter". Applied Physics Letters 89: 051102. doi:10.1063/1.2244042. 
24. ^ Marina, N; Monakov, Y; Sabirov, Z; Tolstikov, G (1991). "Lanthanide compounds—Catalysts of stereospecific polymerization of diene monomers. Review☆". Polymer Science U S S R 33: 387. doi:10.1016/0032-3950(91)90237-K. 
25. ^ C. Wang (200). "In situ cyclization modification in polymerization of butadiene by rare earth coordination catalyst". Materials Chemistry and Physics 89: 116. doi:10.1016/j.matchemphys.2004.08.038. 
26. ^ Xie, Y (2004). "Photocatalysis of neodymium ion modified TiO2 sol under visible light irradiation". Applied Surface Science 221: 17. doi:10.1016/S0169-4332(03)00945-0. 
27. ^ Stengl, V; Bakardjieva, S; Murafa, N (2009). "Preparation and photocatalytic activity of rare earth doped TiO2 nanoparticles". Materials Chemistry and Physics 114: 217. doi:10.1016/j.matchemphys.2008.09.025. 
28. ^ Vinod S. Agarwala, G. M. Ugiansky (1992). New methods for corrosion testing of aluminum alloys. ASTM International. p. 180. ISBN 0803114354. http://books.google.com/?id=0n3cWbIEPpgC&pg=PA180. 
29. ^ Bethencourt, M (1998). "Lanthanide compounds as environmentally-friendly corrosion inhibitors of aluminium alloys: a review". Corrosion Science 40: 1803. doi:10.1016/S0010-938X(98)00077-8. 
30. ^ Takeuchi, M; Kato, T; Hanada, K; Koizumi, T; Aose, S (2005). "Corrosion resistance of ceramic materials in pyrochemical reprocessing condition by using molten salt for spent nuclear oxide fuel". Journal of Physics and Chemistry of Solids 66: 521. doi:10.1016/j.jpcs.2004.06.046. 
31. ^ "Neodymium Chloride". http://www.americanelements.com/ndcl.html. Retrieved 2009-07-07. 
32. ^ "MSDS". https://secure.strem.com/catalog/printer.php?type=msds&catalog_number=93-6022. Retrieved 2009-07-07. 
33. ^ Donald E. Garrett (1998). Borates. Academic Press. p. 385. ISBN 9780122760600. http://books.google.com/?id=imMJJP5T5rsC&pg=PA385.