Thermal degradation of polymers

Thermal degradation of polymers

Thermal degradation of polymers is molecular deterioration as a result of overheating. At high temperatures the components of the long chain backbone of the polymer can begin to separate (molecular scission) and react with one another to change the properties of the polymer. Thermal degradation can present an upper limit to the service temperature of plastics as much as the possibility of mechanical property loss. Indeed unless correctly prevented, significant thermal degradation can occur at temperatures much lower than those at which mechanical failure is likely to occur. The chemical reactions involved in thermal degradation lead to physical and optical property changes relative to the initially specified properties. Thermal degradation generally involves changes to the molecular weight (and molecular weight distribution) of the polymer and typical property changes include reduced ductility and embrittlement, chalking, color changes, cracking, general reduction in most other desirable physical properties. [http://www.zeusinc.com/newsletter/thermal_degradation.asp Thermal Degradation of Polymers - The Zeus Polymer Minute ] ]

The Mechanism of Thermal Degradation

Most types of degradation follow a similar basic pattern. The conventional model for thermal degradation is that of an autoxidation process which involves the major steps of initiation, propagation, branching, and termination.

Initiation

The initiation of thermal degradation involves the loss of a hydrogen atom from the polymer chain (shown below as R.H) as a result of energy input from heat or light. This creates a highly reactive and unstable polymer ‘free radical’ (R*) and a hydrogen atom with an unpaired electron (H*). The strength of the C-F bond means that there it is much harder for thermal degradation to initiate.

Propagation

The propagation of thermal degradation can involve a variety of reactions and one of these is where the free radical (R*) reacts with an oxygen (O2) molecule to form a peroxy radical (ROO*) which can then remove a hydrogen atom from another polymer chain to form a hydroperoxide (ROOH) and so regenerate the free radical (R*). The hydroperoxide can then split into two new free radicals, (RO*) + (*OH), which will continue to propagate the reaction to other polymer molecules. The process can therefore accelerate depending on how easy it is to remove the hydrogen from the polymer chain.

Termination

The termination of thermal degradation is achieved by ‘mopping up’ the free radicals to create inert products. This can occur naturally by combining free radicals or it can be assisted by using stabilizers in the plastic.

The Research Methods of Thermal Degradation of Polymers

TGA

(Thermogravimetric Analysis) (TGA) refers to the techniques where a sample is heated in a controlled atmosphere at a defined heating rate whilst the samples mass is measured. When a polymer sample degrades, it mass decreases due to the production of gaseous products like carbon monoxide, water vapour and carbon dioxide.

DTA and DSC

(Differential thermal analysis) (DTA) and (differential scanning calorimetry) (DSC): Analyzing the heating effect of polymer during the physical changes in terms of glass transition, melting, and so on. [M. A. Villetti, J. S. Crespo,M. S. Soldi, A. T. N. Pires, R. Borsali and V. Soldi. Thermal degradation of natrural polymers. Journal of Thermal Analysis and Calorimetry, Vol. 67 (2002) 295~303] These techniques measure the heat flow associated with oxidation.

Ways of Polymer Thermal Degradation

Depolymerisation

Under thermal effect, the end of polymer chain departs, and forms low free radical which has low activity. Then according to the chain reaction mechanism, the polymer loses the monomer one by one. However, the molecular chain doesn’t change a lot in a short time. The reaction is shown below. [http://nvl.nist.gov/pub/nistpubs/sp958-lide/344-346.pdf] This process is common for polymethymethacrylate (perspex).

CH2-C(CH3)COOCH3-CH2-C*(CH3)COOCH3→CH2-C*(CH3)COOCH3 + CH2=C(CH3)COOCH3

Random Chain Scission

The backbone will be break down randomly, could be occurred at any position of the backbone. The molecular weight decreases rapidly, and cannot get monomer in this reaction, this is because it forms new free radical which has high activity can occurs intermolecular chain transfer and disproportion termination with the CH2’group.

CH2-CH2-CH2-CH2-CH2-CH2-CH2’→CH2-CH2-CH=CH2 + CH3-CH2-CH2’ orCH2’+CH2=CH-CH2-CH2-CH2-CH3

Side-Group Elimination

Groups that are attached to the side of the backbone are held by bonds which are weaker than the bonds connecting the chain. When the polymer was being heated, the side groups are stripped off from the chain before it is broken into smaller pieces.For example the PVC eliminates HCL, under 100-120oC.

CH2(Cl)CHCH2CH(Cl)→CH=CH-CH=CH+2HCl

Oxidation of the polymer

Polyphenylene oxide is well known for oxidation.

ee also

* Chemically Assisted Degradation of Polymers
* Environmental stress cracking
* Indication of weather degradation
* Photo-oxidation process
* Use of stabilisters to enhance weathering resistance
* Weather testing of polymers

References

----


Wikimedia Foundation. 2010.

Игры ⚽ Поможем написать реферат

Look at other dictionaries:

  • Chemically Assisted Degradation of Polymers — is a type of polymer degradation that involves a change of the polymer properties due to a chemical reaction with the polymer’s surroundings. There are many different types of possible chemical reactions causing degradation however most of these… …   Wikipedia

  • Chemically assisted degradation of polymers — is a type of polymer degradation that involves a change of the polymer properties due to a chemical reaction with the polymer’s surroundings. There are many different types of possible chemical reactions causing degradation however most of these… …   Wikipedia

  • Stabilizers for polymers — are used directly or by combinations to prevent the various effects such as oxidation, chain scission and uncontrolled recombinations and cross linking reactions that are caused by photo oxidation of polymers. Polymers are considered to get… …   Wikipedia

  • Polymer degradation — is a change in the properties tensile strength, colour, shape, etc of a polymer or polymer based product under the influence of one or more environmental factors such as heat, light or chemicals. These changes are usually undesirable, such as… …   Wikipedia

  • Photo-oxidation of polymers — Photo oxidation is the oxidation of a polymer surface in the presence of oxygen or ozone that is facilitated radiant energy such as UV or artificial light. This proces is often the the most significant component of weather degradation of polymers …   Wikipedia

  • industrial polymers, major — Introduction       chemical compounds used in the manufacture of synthetic industrial materials.       In the commercial production of plastics, elastomers, man made fibres, adhesives, and surface coatings, a tremendous variety of polymers are… …   Universalium

  • Weather testing of polymers — is the controlled polymer degradation and polymer coating degradation under lab or natural conditions.Just like errosion of rocks, natural phenomena can cause degratation in polymer systems. The elements of most concern to polymers are… …   Wikipedia

  • Differential scanning calorimetry — Differential Scanning Calorimeter Acronym DSC Classification Thermal analysis Manufacturers Linseis Thermal Analysis, Mettler Tol …   Wikipedia

  • Acetaldehyde — Acetaldehyde …   Wikipedia

  • Polymer — Appearance of real linear polymer chains as recorded using an atomic force microscope on surface under liquid medium. Chain contour length for this polymer is 204 nm; thickness is 0.4 nm.[1] A polymer is a large molecule (macromolecule …   Wikipedia

Share the article and excerpts

Direct link
Do a right-click on the link above
and select “Copy Link”